Electronics Forum | Tue Jul 29 14:20:03 EDT 2008 | realchunks
Slight variations should have little impact on your product under normal conditions. All depends on your board.
Electronics Forum | Fri Jul 25 23:01:04 EDT 2008 | chip_flip
What paste are using? You should referance the manufactures time and temperature specification. Running lead-free in a 5 zone oven can be done with out a problem but it is not production friendly. If you are concerned with through put I would look fo
Electronics Forum | Sat Aug 02 08:06:11 EDT 2008 | pcbbuilders
Is there a limit to the time that most components can stay at temperatures around 130-200 deg c? if i slow the time, the first 4 zones will be at this temp for about 5 minutes in no lead process. i am concerned that some chips wont be rated at this t
Electronics Forum | Sat Jul 26 07:42:49 EDT 2008 | pcbbuilders
I am not very concerned about production time, but it is always a thought! Quality is more importnant of course. We have 2 different pastes, with almost identical requirements. We can get close to their profiles, but i am worried that i am spending
Electronics Forum | Mon Aug 04 09:30:16 EDT 2008 | grics
If you have concerns, you can look at the datasheet for each component or contact one of their application or materials engineers and find out what the components are rated for...process-wise. IE, how long can I be in the oven with this part, at what
Electronics Forum | Tue Aug 22 10:06:53 EDT 2000 | George English
Has there been a definite date for the total move over to lead free? Will it be 2004 or 2008. Also is there a direct replacement for leaded solder, I have read various articles on numerous alloys suggested for the switch, such as bismuth, tin, copper
Electronics Forum | Fri Nov 06 02:55:10 EST 2015 | arct1c
Hi, we are looking for 1 or 2 new postreflow AOI machines to replace our old ones and possibly 1 prereflow AOI(we never had pre reflow before). In our company we run low volumes and high volumes. I have been looking at Viscom, Mirtec mostly, Cyberop
Electronics Forum | Tue Nov 10 15:25:37 EST 2015 | 31258
Good morning RedChili, This is Marvin from Saki America. I came across your post and I noticed that you are interested on 3D-AOI and 2D-AOI machines. We can offer pre-reflow and post-reflow full 3D-AOI and 2D-AOI for you needs. IF you have any ques
Electronics Forum | Fri Nov 06 07:46:33 EST 2015 | clampron
Good Morning RedChilli, I have worked with Mirtec for quite a few years. I have looked at some of the other machines mentioned but have no practical experience with them. I started with the Mirtec MV-2 (long ago)due to the success of this platform,
Electronics Forum | Tue Jan 31 10:59:55 EST 2006 | carterhoward
Hi All, I�ve been doing some research on the issue of running lead-free solder paste and leaded solder paste through reflow at the same time. The point with this would be to process all standard leaded components with Lead paste while also processi