Electronics Forum | Thu Sep 07 11:02:29 EDT 2000 | Travis Slaughter
Maybe its not splatter, in my experience a sloppy operator can get paste on contacts and just one sphere can rune them and can look like splatter.
Electronics Forum | Fri Sep 08 00:24:35 EDT 2000 | Jim Arnold
Sudden flux boil will cause splatter. More thorough drying or a slower intial ramp to allow drying to occur before a boil or "splatter" temperature is reached may aid your problem.
Electronics Forum | Mon Jun 27 09:09:19 EDT 2005 | Bob R.
We've all been soldering Pb free parts for a couple decades. All your surface mount capacitors have probably had a Sn finish for years. Whenever one of our parts with a SnPb finish converts for Pb free we have the manufacturing site do a small buil
Electronics Forum | Tue Nov 06 22:37:35 EST 2012 | davef
Ryan ... "As for bismuth-based lead-free alloys, a lower melting temperature than that of tin-lead is offered together with a cost similar to that of tin [in the area of $3/lb]. Unfortunately, bismuth in soldering alloys tends to create embrittlemen
Electronics Forum | Thu Nov 15 03:07:35 EST 2012 | nikyta
Thanks for your reply. As already said by Anvil1021, is not a good idea to mix Lead and Bismuth! Stay away from Bismuth if you have even the slightest traces of Lead on yours PCB, stencil, squeegee, spatula, blade, cleaning paper or cleaning cloths,
Electronics Forum | Thu Sep 05 23:18:03 EDT 2013 | feiyangniao
There is a new toy I received today: a NeoDen TM-240A automatic desktop pick and place machine! I’ve kept my eyes on this baby for a quite a while, and finally decided to make a purchase last week. The shipping was very fast: DHL from China, a total
Electronics Forum | Fri Nov 02 09:09:56 EDT 2012 | davef
Sure you can use it it with leaded HASL. Recognize that ... * Your Sn42/Bi58 will no linger be Sn42/Bi58 * Your leaded HASL will no longer be the same leaded HASL that walked in the door to your plant * Lead from HASL coatings can diffuse through the
Electronics Forum | Mon Sep 23 18:11:10 EDT 2002 | steveb
On an assembly reflowed in air saw the same thing: 0201's with a grainular solder joint, but 0402's and above with perfectly formed joints. Reflow profile all within acceptable tolerances. Reflowing in nitrogen solves this problem, but increases t
Electronics Forum | Tue Feb 19 16:19:26 EST 2008 | edatasys
Check out http://www.solderstar.co.uk/wavePro.html This tool measures all key wave solder information with a single pass. Wave/PCB contact, immersion depths, etc. Also has a reflow pack to allow use on reflow, 9 channels with predictive software. B
Electronics Forum | Mon Mar 26 09:41:03 EDT 2018 | fuji_user_2014
Hi Gurus, Looking for alternatives to line makeup after reflow oven. Currently, I have a continuous on flat belt conveying out of my reflow oven straight to an EOL bench. The operator manually picks up the board off the belt (there is a roller at t