Hi Guys,recently i am facing an issue. Refer to the attached photo. This PCB is high RF speed, gold immersion single layer. After reflow, my solder seems to have black stains on it. I tried with SAC305 paste water soluble and no-clean, both results a
Electronics Forum | Fri Dec 27 11:42:18 EST 2019 | emeto
I could not see pictures of your board - please attach one or two. So to answer your questions: 1. wave should not overflow over your board - mostly we use pallets as carriers to protect the assembly. 2. Solder dross is caused because your wave is no
Electronics Forum | Fri Dec 27 17:40:55 EST 2019 | rgduval
Using no-clean flux will make the boards very difficult to clean. If you can switch to water soluble flux, your life will be much easier. The "icicles" lead me to think that the board isn't getting hot enough in the pre-heat cycle, and/or there isn
Electronics Forum | Fri Dec 27 12:42:36 EST 2019 | rgduval
In your video, it looks to me as though the bottom of the glass is too low, but, I can't tell for certain. As a general rule, keep the top of the wave no higher than the mid-point of the PCB. Top flow will take care of itself thanks to flux and cap
Electronics Forum | Thu May 27 22:29:14 EDT 1999 | Mike Flori
Does anyone have a suggestion for a UV resistant black potting material? The material recommended by a local vendor turned gray in a couple of months in the sun here in Florida. We are using L.E.D.'s in a small housing (about 1.2" cube) and need to s
Electronics Forum | Fri Dec 27 16:12:54 EST 2019 | anteiv
thank you for reply here is picture of the board https://imgur.com/a/i2MfFBw on the bottom are pins/components which height is about 3-4 mm from bottom of the board we had to increase distance of board from nozzle to make clearance and we increas
Electronics Forum | Tue Aug 02 15:03:37 EDT 2016 | davef
On a previous black pad experience we soldered a wire to a fiducial and did a pull test to failure. On the black pad board the wire and solder pulled of clean leaving the fiducial on the board. On good boards the copper came off with the wire. If you
Electronics Forum | Fri May 28 11:14:21 EDT 1999 | TONY MASTROIANNI
| Does anyone have a suggestion for a UV resistant black potting material? The material recommended by a local vendor turned gray in a couple of months in the sun here in Florida. We are using L.E.D.'s in a small housing (about 1.2" cube) and need to
Electronics Forum | Fri May 28 11:22:21 EDT 1999 | TONY MASTROIANNI
| Does anyone have a suggestion for a UV resistant black potting material? The material recommended by a local vendor turned gray in a couple of months in the sun here in Florida. We are using L.E.D.'s in a small housing (about 1.2" cube) and need to
Electronics Forum | Fri May 28 12:51:11 EDT 1999 | John Thorup
| Does anyone have a suggestion for a UV resistant black potting material? The material recommended by a local vendor turned gray in a couple of months in the sun here in Florida. We are using L.E.D.'s in a small housing (about 1.2" cube) and need to