Electronics Forum | Fri Oct 08 16:48:24 EDT 1999 | Charles Morris
| I recently had the opportunity to visit the vendor who is making my boards. On my trip I noticed that the guy who was in charge of the SMD placement machine (brand new Samsung) still had to manuallly place about 20%-40% of the parts after placement
Electronics Forum | Thu Aug 06 12:49:41 EDT 1998 | justin medernach
| I am looking for advice or information from anyone about the possible reliability problems associated with epoxy on solder pads of discrete devices. Will the epoxy expand and lift over time, Will there be adverse reaction between the solder and the
Electronics Forum | Fri Aug 07 01:02:51 EDT 1998 | zeek - just wanna to get a word in here
| | I am looking for advice or information from anyone about the possible reliability problems associated with epoxy on solder pads of discrete devices. Will the epoxy expand and lift over time, Will there be adverse reaction between the solder and t
Electronics Forum | Wed Apr 04 17:40:39 EDT 2007 | davef
Rob: How do you rework blow-holes and pin-holes? PTH plating thickness SB 1 thou or greater. Epoxy is hydroscopic. So, you should control the environment and/or bake the moisture from the boards before soldering. Search the fine SMTnet Archives f
Electronics Forum | Tue Feb 08 16:09:09 EST 2000 | dean
Generally speaking with most electronic grade epoxies: 1. Cure time is a function of temperature. 2. Polymer bonds begin to quickly break down above certain temperatures (product specific). I believe aprox 170-180C. The strength of the bond de
Electronics Forum | Wed Sep 21 20:03:34 EDT 2005 | kevinbooth
I am going to agree with Rob a little. It is also possible that a internal ground plane might be under or connected to the pads of this cap thus causing a increase in temp to this part during reflow. This can cause parts on occasion to jump from the
Electronics Forum | Thu Jun 24 10:48:02 EDT 1999 | Earl Moon
| Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody hel
Electronics Forum | Thu Mar 01 21:20:47 EST 2007 | J.R.
Let's talk pin holes and blow holes. I've been here since the transistion of leaded to lead-free process started for our company and we purchased a wave machine just to keep up with our lead-free orders. we put out 500-1000 boards a day both leaded a
Electronics Forum | Thu Jun 17 11:18:03 EDT 1999 | Ian Clelland
| | | | | | Our company is experiencing cracked caps at our pick and place operations. The caps are being placed onto epoxy dots for subsequent wave solder operations. At present, be have set the pressure of the head at 2 in/lbs. This being down fr
Electronics Forum | Wed May 26 10:00:03 EDT 1999 | David Scott
| | | | | | | | | | | | Any suggestions on how to maintain Adhesive dispensing nozzles??? They seem to plug up over night and it is starting to get on my nerves. We have tried leaving the nozzles in the machine, removing them and soaking in alcoh