Hi, We are in the process of transitioning to LF production. What are some of board materials being successfully used in production? Also, what surface finishes show promice of good results with SAC 305 solder? We are currently testing multiple boar
Electronics Forum | Fri Jun 18 12:50:32 EDT 1999 | jseagle
We currently use HASL on all of our boards and I would like to move to something else. I have sampled some boards with Entek OSP and I loved it, the problem is we have plated mounting holes on just about every board we make. Does anyone have inform
Electronics Forum | Fri Jun 18 13:48:37 EDT 1999 | Earl Moon
| We currently use HASL on all of our boards and I would like to move to something else. I have sampled some boards with Entek OSP and I loved it, the problem is we have plated mounting holes on just about every board we make. Does anyone have info
Electronics Forum | Wed Oct 30 04:07:37 EDT 2019 | pate2418
Dear colleagues. Share your experience, please. Printed circuit boards with which finish surface do you prefer to mount? Which finish surface in your experience is preferable and why.
Electronics Forum | Tue Dec 07 17:38:50 EST 2004 | davef
ANSI/J-STD-003 - Solderability Tests for Printed Boards is widely accepted. That's it, that's the list. If you email us your email address, we'll give you someone to call. Without knowing the number of boards that you plan to run across your wave,
Electronics Forum | Mon Nov 04 07:31:54 EST 2019 | amitthepcbguy
As a manufacturer, I prefer plated nickel gold, electroless nickel immersion gold, immersion silver and palladium. These surface finishes are the best options to replace leaded surface finishes. These surface finishes can withstand higher temperature
Electronics Forum | Mon Nov 04 14:56:35 EST 2019 | stephendo
I think it might be the best choice for OEMs that only run one finish and practice JIT. (taking cost into account) For everyone else I think they will eventually run into trying to use them too long after they have been opened. But when you can run b
Electronics Forum | Thu Dec 14 10:14:04 EST 2000 | PeteB
Jacqueline, Asuming you mean immersion silver: Advantages - Very flat finish compared to HASL, more easily solderable than bare copper with OSP and more process tolerant than this in our experience, reasonable shelf life, cheaper than immersion gol
Electronics Forum | Thu May 02 11:34:39 EDT 2002 | Yannick
Hi, You can go to http:\\www.circuitree.com they had a supplement with the april issue of the magazine with a very good article on 4 board finish, if you are able to find it on the web site you will find all your anwser and more :)The article name
Electronics Forum | Thu May 02 23:06:56 EDT 2002 | sohct
Hi Yannick Please sent the article "Board finishes for EMS Provider" to me as I can't find it in Circuitree. Your help is very much appreciated. Regards