Electronics Forum | Fri Jan 15 14:45:48 EST 1999 | Earl Moon
| | | Folk's, | | | | | | I'm looking for information of how long you cna store a gold finish PCB before building it. I know there are problems with the gold disappearing into the underlying nickle over time / temperature etc but exactly how long do
Electronics Forum | Mon Jan 18 10:01:16 EST 1999 | John W
| | | | Folk's, | | | | | | | | I'm looking for information of how long you cna store a gold finish PCB before building it. I know there are problems with the gold disappearing into the underlying nickle over time / temperature etc but exactly how l
Electronics Forum | Tue Jan 19 11:12:41 EST 1999 | Dave F
| | | | | Folk's, | | | | | | | | | | I'm looking for information of how long you cna store a gold finish PCB before building it. I know there are problems with the gold disappearing into the underlying nickle over time / temperature etc but exactly
Electronics Forum | Wed May 30 10:09:39 EDT 2012 | brettrenishaw
Recently we have noticed a purple-blue colour film on the surface of the molten solder. It can be cleared when de-drossing the pot. The pot will normally go a yellow/gold colour before it turns purple-blue. Is this most likely an oxide of the tin or
Electronics Forum | Thu Aug 28 23:15:44 EDT 2014 | phyllishwl
Hi all, Our production reported that they found 3 panels out of 53 panels with strange phenomenon after reflow. 1/ Blister / Delamination of PCB panels, 2pcs blister/delamination under solder mask, 1pc under Gold plating at Gold finger 2/ Silkscr
Electronics Forum | Fri Sep 14 02:18:32 EDT 2001 | gsparka
Hi. After reflow soldering. There are lots of non wetting of leads. 71 b'd all are mounted resister,condensor,qfp,plcc,bga have got the defects so many. all defecs occured in the fine pitch ic. others are good. On some fine pitch pads not mou
Electronics Forum | Mon Feb 05 10:21:21 EST 2007 | davef
Thermal conductivity [W/m-�C] * Silver: 418 * Aluminum: 403 * Copper [rolled annealed]: 392 * Copper [electrodeposited]: 392 * Gold: 297 * Nickel: 90.7 * Tin: 73 * SAC: 73 * Castin: 57 * Pb37Sn63: 51 * Lead: 35 * Epoxy, phenolic: 25-75 * Conformal co
Electronics Forum | Mon Apr 27 14:39:38 EDT 2015 | davef
Anirudh: When board fabs talk "surface finishing" they're talking about the solderability protection that you'd like on the solderable copper component mounting pads that you laid-out for each component: * Bare copper pads corrode very quickly * Corr
Electronics Forum | Mon Nov 27 19:32:02 EST 2000 | Michael Parker
Prof. Whoopee - amazing facts that you find on your 3-D BB, it has completely confounded my comrade, Chumley. Plainly spoken that around the SF Bay Area a.k.a. Silicon Valley(ever hear of the famous SF Fog?)during the winter months, near the coast a
Electronics Forum | Sun Apr 18 14:26:36 EDT 1999 | Steve Gregory
| | Please visit our Web site, especially 'link page', to get some hint for roll typr of cleaning wiper for automatic screen printers. http://www.squeegee.co.kr | | | Idiot: I wouldn't visit your site if I had to start using toilet paper. Keep yo