Electronics Forum | Fri Jan 19 10:43:28 EST 2007 | jimmyjames
You guys are all joking right?! There aren't any contaminates in your solder, the different colors on the surface are completely normal and even expected. The top layer of solder oxidizes and the structure of the surface resembles crystals, refract
Electronics Forum | Wed Aug 30 05:36:38 EDT 2017 | alexandrdmc
Set of 5 with a WHITE SATIN RIBBON & GOLD GLITTER encased in the lettering. Bride to be, Mother of the Bride, Chief Bridesmaid, Mother of the Groom, Bridesmaid. A unique set for the bride, mother, girlfriend, groom. Decorate any party. Size fits all.
Electronics Forum | Sat Nov 14 08:05:54 EST 1998 | Earl Moon
| | | | I believe that gold fingers on my circuit boards are being | | | | contaminated and need to clean them with some chemical | | | | solution. Any recommendations. | | | | | | | Chuck: What is the type and source of your contamination? Dave
Electronics Forum | Tue Apr 19 16:20:05 EDT 2016 | davef
Don't blame it on the poor paste thickness requirement [although I might go on to argue that it's could be a contributor to the issue]. Most likely you're the problem. About 70% of the time solder on gold fingers is caused by poor cleaning of screen
Electronics Forum | Mon Aug 31 21:47:56 EDT 2009 | davef
In response to your question: 3 Saponifier / non saponifier 3a Saponifiers: * Aqueous Technologies: PCB-Wash http://www.aqueoustech.com * Kyzen: XJN http://www.kyzen.com * EnviroSense: Enviro Gold #816 http://www.envirosense-inc.com 3b Non-Sapo
Electronics Forum | Mon Aug 27 22:16:03 EDT 2012 | ilanhovan
Hi, my supplier is using the same Aqueous machine to clean the boards for 2 different customers. My product uses the chemistry of leaded clean flux meanwhile the other product uses the chemistry of lead free with no clean flux, however that product r
Electronics Forum | Mon Sep 22 17:02:58 EDT 2008 | hegemon
You are on the right track Ismir. Essentially however, as the programmer of the machine, I am the one that creates the PCB with the errors to benchmark the settings for the machine. No secret lab though! :-) Easy enough for most any AOI machine to
Electronics Forum | Thu Feb 19 12:35:13 EST 1998 | Earl Moon
| | We are currently investigating alternatives to HASL for circuit boards with 20 mil pitch smt pads and below. If you have experience with this product or simular immersion tin products with respect to manufacturing or assembly I am very interest
Electronics Forum | Thu Dec 18 23:44:53 EST 2003 | Dean
...don't expect high yields with hasl on that device. Yeah, you an do it. But not reliably. Also, factor in board warp, bump tolerance AND HASL variation....recipe for disaster. can your process toleate a selective gold on the one device? How ab
Electronics Forum | Mon May 12 12:58:07 EDT 2014 | emeto
Hello all, I have a diode(gold plated)on some assemblies that gives me a a hard time. The paste is wetting too good and climbs the lead of the component and touches the body which is a defect. I just wonder what if there is a way to heat the board e
.png)