Electronics Forum | Tue Jul 08 12:04:31 EDT 2008 | patrickbruneel
Military is outside the scope of the directive. The RoHS directive is mainly focused on electronic equipment with a high potential to end up in the normal waste stream such as consumer products. The EU commission also knows that removing lead from a
Electronics Forum | Mon Aug 04 16:20:35 EDT 2008 | patrickbruneel
After analyzing the pictures I don't think the solder balls are caused by the solder mask. If the problem would be solder mask related the solder balls would only show up on the solder mask but there are also solder balls on the plastic tabs. To me i
Electronics Forum | Wed Aug 20 08:23:36 EDT 2008 | davef
Your tantalum capacitor supplier offers the best advice. We're not sure of the package that you plan to use. * If you are referring to molded package, surface mount, tantalum caps, yes, they can be wave soldered. Smaller case size chips (eg, Kemet A
Electronics Forum | Wed Aug 27 14:19:40 EDT 2008 | grics
Have you given this information to your paste manufacturer???(Profile, Pics of defects?) The profile seems to look ok(without knowing paste info...) I think the ramprate looks a little aggressive but it could be the scaling of the profile and the i
Electronics Forum | Tue Nov 04 07:50:14 EST 2008 | davef
Sure. Here's what you should do to apply repeatable amounts of flux on BGA during rework: * Squirt some gel flux on a plate or something like that that has a flat bottom and raised sides to corral the flux. * Cut notches into one edge of an old credi
Electronics Forum | Fri Nov 14 08:06:43 EST 2008 | jdengler
Have you figued out how to import the gerber data into Camtastic? Once that is done click the tool menu at the top then the assembly utilities then create and group parts. This will allow you to select the pads for a given package and name it the
Electronics Forum | Mon Dec 01 12:39:06 EST 2008 | tsvetan
this is really nice one ;) paper and cotton have lowest potential to generate static electricity see below, and usually is good practice to wear cotton glowe at least to one of your hands to not leave greasy finger spots on the gold finish of the PC
Electronics Forum | Thu Dec 11 04:25:06 EST 2008 | lconnor
I have previously experienced dispensing glue dots using a camalot system. This was used to dispense dots for a variety of components, as the SMT was applied post through hole and then wave soldered. No paste was used in the process. The other benefi
Electronics Forum | Wed Jan 28 21:47:56 EST 2009 | padawanlinuxero
Hello! I am having trouble with the new changes from lead joint to lead free joint, we are working on change to lead free, I am using a 3 zone oven reflow, the zone temps are : zone 1 zone 2 zone 3 (top and bottom) 128 208 260 th
Electronics Forum | Fri Jan 30 06:28:42 EST 2009 | gregoryyork
Hi Armando Hotflow 7 is a big machine and one of the best Reflow ovens around (in my opinion), well suited for Lead Free. A typical 1.6mm board has the following settings for Lead Free SAC305 paste All Temperature settings are Top and Bottom Prehea
winsouce.jpg)