Electronics Forum | Fri Dec 31 10:16:22 EST 2004 | Brad
Can anyone recommend a company thats local to New England that does extensive solder joint analysis.
Electronics Forum | Wed Feb 21 15:33:10 EST 2007 | wavemasterlarry
sure sounds like a lot of busy work just to make solder joints for a vacuum cleaner.
Electronics Forum | Tue Jun 25 09:45:39 EDT 2019 | edhare
See also ... https://www.semlab.com/solder-joint-failure-modes/
Electronics Forum | Wed May 17 12:22:09 EDT 2006 | russ
What color is the pad? coated with solder?, black?, still gold? Russ
Electronics Forum | Wed May 17 12:31:54 EDT 2006 | Mark
Hi , It looks like there is solder (shiny like mirror surface). Defently not black and not gold. Regards Mark
Electronics Forum | Thu May 18 10:28:46 EDT 2006 | slthomas
Are you seeing added solder or is it possible you're looking at nickel?
Electronics Forum | Sun Jun 10 11:08:26 EDT 2001 | nifhail
I know that there is no pre-defined strength for the solder joint as it will depend on solder volume deposited, pad geometry, lead component's lead solderability etc. but, what would be the best ball park for the good joint for 0402, 0603, 20 mil pti
Electronics Forum | Fri May 31 05:54:09 EDT 2019 | dhanish
What are the common cause for solder joint crack after the pcba go through Temperature cycling test ?We have seen failure on solder joint for the memory part.
Electronics Forum | Mon Apr 04 17:32:07 EDT 2005 | toromaster
we also have a need to measure the solder bond strength of our gull wing parts on our pwb. there are many published comparisons between eutectic SnPb and no Pb solders out there. the number that comes to mind is about 10N to 15N. I have not looked
Electronics Forum | Thu Mar 24 19:17:43 EST 2005 | EA
Hi, We are running the automotive product and question was throw to us how do we ensure that our solder joint are good enough after reflow.....and during the sealant process, there's a bit of bend on the nozzle and it toughes the component and custo