Electronics Forum | Tue Feb 23 11:29:18 EST 1999 | Bill
No salesmen please. (I didn't use my real email address) I would like to know if anyone is using either of these SMT machines and if they are what input can you give me on them. We are looking at the Contact 3Z and the Multitroniks DHM for our low
Electronics Forum | Mon Mar 01 16:11:24 EST 1999 | Innovative Concepts
For as much as you can minimize bridging in these condition by changing board orientation, the only way to eliminate them may be to add debridging airknife tech to your system, or purchase a system that is fitted with this technology. We have been t
Electronics Forum | Tue Feb 23 03:44:51 EST 1999 | K
| Can anybody give me the Pros and Cons of of using Cartridges over jars and/or vice-versa. Also, if using cartridges, what is the best way to keep the paste from seperating, short of buying a mixer that cost over $5000.00 | Thanks, | Bill | Inter
Electronics Forum | Thu Feb 18 21:20:13 EST 1999 | Ernie Flamont
During inspection and test we find leads which do not get soldered. Some are because of insufficient paste, but with others everything looks right. This will only happen on 1 to 2 pins, and it is not isolated to a specific type of ic or location on
Electronics Forum | Thu Feb 18 20:24:37 EST 1999 | Tony
I'm trying to replace the PTH connectors with the SMT connectors in my design, and would like to make sure the SMT connector solder joints are as stong as PTH's. What's the right test to verify that? Is Pull and Shear test is the right choice? Where
Electronics Forum | Wed Feb 10 07:50:52 EST 1999 | michele sommaruga
I am referring to reflowing twice. Fist time I reflow the up side, turn the PCB and reflow the bottom side. | By double reflow are you referring to double sided reflow? Or are you referring to reflowing twice? | | | | I would like to have informat
Electronics Forum | Thu Feb 04 09:09:07 EST 1999 | dave
Can anyone help me with the pros and cons of trying to wave solder tantalum and large (1812) ceramic capacitors. I do know that one may see fractures on larger cermaic caps, but have not seen much on the tantalums. Any insight as to what problems I c
Electronics Forum | Sun Jan 24 10:49:38 EST 1999 | Ng
It has been known that sufficient cooling after soldering is important in order to get a stronger joint during its solidification stage. And it has been so much emphasised with reflow oven. But, why many models of wave soldering machine do not come w
Electronics Forum | Sat Jan 23 12:37:35 EST 1999 | parag palshikar
hi, i am working towards developing a no-clean process for a customer at contract manufacturing facility. the assemblies have gold fingers on them. these are masked to prevent from any damage to them during reflow soldering. the earlier process ut
Electronics Forum | Sun Jan 17 13:31:28 EST 1999 | greg cronin
I am trying to program some tant caps on my universal 4785 chipshooter and it just won't take. If anyone has any experience with the 4785 please let me know. I have programmed some pretty tough parts in the past and I know the vision on the 4785 c