Electronics Forum | Thu Mar 25 13:53:28 EST 1999 | Bob Willis
| | | Your problem may be related to silver migration (leaching) into the solder. I had what seems to be a similar problem. The solution was using solder with 2% silver content. See these pages for a bit more information: | | | | http://www.ferr
Electronics Forum | Thu Oct 18 18:39:15 EDT 2001 | davef
Responding to your questions ... RELIABILITY OF 1% SILVER SOLDER PASTE: It�s as good as the next solder paste, all other things the same. Look at your back articles by Jennie Hang in SMT magazine. I want to say she wrote an article on the topic i
Electronics Forum | Tue Jul 04 16:13:09 EDT 2000 | TOOLMANTIM
HELLO BILL I HAVE SOME QUESTIONS FOR YOU 1:HOW ARE YOU CLEANING YOUR STENCIL 2:ARE YOU SINGLE OR DOUBLE PRINTING. 3:ARE YOU USEING VACUUM FIXTURES OR NOT? HERE ARE SOME OTHER THINGS TO TRY. IF YOU ARE CLEANING YOUR STENCIL OFTEN BECAREFUL OF USEING