Electronics Forum | Sat Oct 06 09:01:51 EDT 2001 | davef
In the fine SMTnet Library, there is a "Terms & Definitions" section that covers CEM-3 and similar items.
Electronics Forum | Fri Jun 04 01:13:31 EDT 2010 | boardhouse
Hi fotis, Big difference between Cem3 & FR4 is that FR4 the glass is woven and Cem3 is sheet glass non-woven. for Multi layer product, i would not consider Cem3 due to increase chance of de-lam due to lack of weave for strength. Cem1 and Cem3 are
Electronics Forum | Wed Aug 26 12:02:23 EDT 1998 | Steve Joy
Does anyone have any experience they are willing to share on Ag epoxy used as a copper through hole plating replacement? Was CEM3 used? What are the limitations? Thanks, Steve
Electronics Forum | Tue May 25 13:30:38 EDT 2010 | nikopolidis
HI Please Advice witch material can stand more heat FR4 or CEM3. PCB assembly will be used under the body of toaster Temp. range 90°C Could anyone tell me the difference in PCB material For imcoming quality control. Thanks & regards Fotis
Electronics Forum | Fri Jun 04 11:28:15 EDT 2010 | mikesewell
At 400C, I'd worry about the solder as well....
Electronics Forum | Wed Jun 23 07:24:55 EDT 2010 | szpcbpartner
welcome to PCB Partner, there are more than 2300 PCB suppliers here. http://www.pcbpartner.com
Electronics Forum | Fri Aug 28 23:32:39 EDT 1998 | Pete Sorenson
| Does anyone have any experience they are willing to share on Ag epoxy used as a copper through hole plating replacement? Was CEM3 used? | What are the limitations? | Thanks, | Steve I have used silver epoxy extensively for conductive bonding applic
Electronics Forum | Thu Aug 27 17:40:11 EDT 1998 | Earl Moon
| Does anyone have any experience they are willing to share on Ag epoxy used as a copper through hole plating replacement? Was CEM3 used? | What are the limitations? | Thanks, | Steve Steve, Hello again. Hope you guys (Intel) aren't going to do that