Electronics Forum | Mon Jun 21 02:15:03 EDT 2010 | ppcbs
We also encountered the crack case in multi layer Ceramic Cap,0603 after touch up. Most failure were on the terminals. Previously, we used 0805 instead 0603.that time, failure were very few.
Electronics Forum | Tue Jun 22 08:37:52 EDT 2010 | davef
Dennis: These "terminal detach failures" probably are caused by thermal shocking of the components. * Preheat the components * Use a hot air pencil rather than a soldering iron
Electronics Forum | Sat Jun 19 00:49:17 EDT 2010 | mun4o
Hi all, lately ofen I have problem with cracked ceramic capacitors.We use 0805 and 0603 cap. Samsung.ICT measure diferent capacity of nominal.If I tray to desoldering component , then component cracked.I think , that the reason is the moisture in com
Electronics Forum | Fri Jun 25 05:34:40 EDT 2010 | ppcbs
Hi iv40 Try with NIC ceramic capacitor that was tested in wet process. We hav succeed with these cap after we found some failure with Kemet ceramic Cap which tested in dry test process while manufacturing.
Electronics Forum | Wed Jun 23 08:47:32 EDT 2010 | mun4o
Hi, about location - components are in the diferent location on PCB.In the one PCB have 7 cap 560pF 0603 , and some of thenm are cracked, another are OK. When I look at 20x microscope , I can't see defect, but ICT measure from 200 to 350pf.When hea
Electronics Forum | Fri Jun 25 09:18:23 EDT 2010 | flipit
Thanks, Dennis. That is a good idea, but I > have problem :) - our logistic department lookig > for cheap components...What other mnfg of cap you > use? Regards, The capacitor dielectric material might be something you could look at also. COG,
Electronics Forum | Fri Jul 09 19:09:52 EDT 2010 | rway
A couple of things: Does the cap break if you try to remove it with hot air? If not, than you are breaking the caps do to mechanical stress. We have had similar issues. I don't think your board is suffering from mechanical stress from depaneling o
Electronics Forum | Wed Jul 10 18:19:42 EDT 2002 | davef
Flex cracking under the terminations is generally regarded as one of the primary causes of failure of ceramic chips. If you can see cracks in the solder joints from board flex, those chips are certainly strongly suspect, and you must assume there is
Electronics Forum | Fri Apr 18 16:53:25 EDT 2003 | takfire
DST, What was the crack signature? Was the crack parallel with the internal electrodes or 45� with the terminal electrode? It is also important to determine the orientation of the failed caps on the PCB (in regards to depaneling). Perhaps the cap
Electronics Forum | Mon Jun 30 10:52:36 EDT 2003 | Bob
Suggest you ask vendor for a failure analysis. Ceramic chips have specific signatures for mechanical or thermal shock cracking. The vast majority of failures are due to mechanical flex. Depanelization and secondary operations such as hand insertion