Electronics Forum | Mon Aug 09 07:13:08 EDT 2010 | raghu
We have PVA 354Bench top conformal coating machine. We are going to procure the Humiseal 1B31 material. Is this material is suitable for this model of machine? Is there any special pecautions to be taken while programming? What are the main problemsd
Electronics Forum | Tue Aug 10 01:02:31 EDT 2010 | raghu
We have PVA 354Bench top conformal coating machine. We are going to procure the Humiseal 1B31 material. Is this material is suitable for this model of machine? Is there any special pecautions to be taken while programming? What are the main problems
Electronics Forum | Fri Dec 18 09:27:51 EST 2009 | sforman1
Tom: Once again - why are you using solvent based conformal coating. 1B31 is OK as a CC but it contains Toluene and MEK!! It is only 35% solids which means you are trying to get rid of 65% solvent. If you must use it due to customers requirement then
Electronics Forum | Wed Feb 23 22:38:28 EST 2005 | davef
We: * Cure 1B73 according to spec in a heat box, like a Blue-M * Clean nozzles [one set in use, one set being cleaned] in thinner in a bronson ultrasonic cleaner * Haven't evaluated coatings in years, but would do it according to J-STD-001C, Reqmnts
Electronics Forum | Thu Feb 17 15:01:23 EST 2005 | davef
We're not familiar with your DYMAX #984-LVUF. The problem is not with your conformal coating. The problem is with your 0805 [and not all of 0805, probably just those from a specific supplier]. This lack of coverage of components is called dewetting
Electronics Forum | Thu Mar 08 01:19:16 EST 2001 | Mike Moninger
The environment essentially defines the need for coating. "Inside" may mean inside a men's locker room with attendant high humidity or inside a climate-controlled clean environment. Conformal coatings offer protection against moisture, fungus, chemi
Electronics Forum | Wed Oct 27 13:20:47 EDT 2004 | DavidB
We are producing boards with Alpha 591S RMA No-Clean paste and are coating after SMC with Dow silicone ( toluene solvent based) conformal coating. We have experienced several failures due to soft shorts ( electrochemical migration?) We have also obse
Electronics Forum | Wed Feb 23 10:01:00 EST 2005 | frankracine
Dave, Few questions concerning your Umiseal 1B73. To cure your Acrylic coating do you respect specification ( 2Hrs-170degree F) or you go faster than that? What do you use to cure it? Do you have to clean your nozzles each day or each monday beca
Electronics Forum | Sun Apr 10 03:25:35 EDT 2005 | Peter
Normally, some conformal coatings do not have very good wetting properties, that should be basic function of a good coating material (the same reqirement as avoid bubbles during coating process)! For UV curing conformal coatings, you can try Lackwe
Electronics Forum | Fri Sep 11 12:08:10 EDT 2015 | derrikf
I built one using an old Asymtek Automove. When all was said and done, it cost less than $400, including what was paid for the machine itself. It's a very basic setup, (air over syringe), but for our needs it does everything and more. With air to syr