Electronics Forum | Wed Aug 10 07:55:21 EDT 2005 | ajaydoshi
we are using heareous F381, F352 no clean solder paste. specially in qfp for high frequency board we observe that cleaing / removing of ' no clean flux 'is require. if we do not clean same most of time after all test & envioumental test it shows pin
Electronics Forum | Wed Aug 10 08:10:39 EDT 2005 | davef
Comments are: * Sounds like it's necessary to clean "heareous F381, F352 no clean solder paste" in your application. Consider a paste that may be better suited to your application. * If you're cleaning "low residue flux", consider using an organic ac
Electronics Forum | Wed Aug 10 08:53:45 EDT 2005 | jh0n!
Wasn't aware of that. We're using a no-clean with RF pcbs, and that's something to bear in mind for the future - thanks.
Electronics Forum | Wed Aug 10 17:19:24 EDT 2005 | Steve Stach
The propensity for flux residues to cause shorts can be increased in humid environments where water molecules hydrate the surfaces. At high frequencies, electrons travel on the surface of conductors/insulators, increasing the likelihood of shorts in
Electronics Forum | Mon Oct 22 15:41:39 EDT 2007 | davef
Bruno The real question about your troop using Kester 951 wave solder flux on boards is: how is the flux applied and controlled. See, when you apply this flux with your wave solder fluxer, it is ideally applied in a metered fashion with your fluxer
Electronics Forum | Wed Feb 26 22:22:00 EST 2003 | Grant Petty
Hi, The guys here have some boards that have been reworked however as we use no-clean paste we are getting the white residue after ultrasonic cleaning. We are using an alcohol based cleaner in the ultra sonic cleaner. Does anyone have any ideas, or
Electronics Forum | Tue Sep 02 14:59:41 EDT 2008 | hermes
if two boards with different solder masks give different results on flux residue level after soldering with the exact same machine settings than it is clear that one of the solder masks is not compatible with your no-clean flux. could be the solder m
Electronics Forum | Thu Aug 28 11:31:17 EDT 2008 | patrickbruneel
Matt solder mask finishes gives the widest process window in view of potential amount of residues when using No-Clean. Shiny (glass like) finishes are more sensitive to residues due to lower surface area compared to matt finish. If the shiny finish i
Electronics Forum | Wed Aug 27 15:49:43 EDT 2008 | grics
I think WML ought to have some photos on how to do this...
Electronics Forum | Wed Aug 27 22:54:44 EDT 2008 | omid_juve
what is WML ? can you please explain more