Electronics Forum | Mon Aug 09 07:13:08 EDT 2010 | raghu
We have PVA 354Bench top conformal coating machine. We are going to procure the Humiseal 1B31 material. Is this material is suitable for this model of machine? Is there any special pecautions to be taken while programming? What are the main problemsd
Electronics Forum | Tue Aug 10 01:02:31 EDT 2010 | raghu
We have PVA 354Bench top conformal coating machine. We are going to procure the Humiseal 1B31 material. Is this material is suitable for this model of machine? Is there any special pecautions to be taken while programming? What are the main problems
Electronics Forum | Thu Oct 08 08:15:39 EDT 2009 | kpm135
We've used both 1A33 urethane and 1B31 acrylic coating on our SMT assemblies with great success for many many years. This is with components of all shapes and sizes including a 9 ball micro-BGA. We apply the coating in every way imaginable and we hav
Electronics Forum | Mon Dec 27 10:03:35 EST 2010 | duso02
Contact your distributor for the coating or Humiseal directly. Humiseal has had a recent issue with batches of 1B31. The specific problem is lack of adhesion, which is what you have as well. You need to find out if your batch # is one of the affected
Electronics Forum | Wed Mar 04 10:05:13 EST 2020 | dontfeedphils
In a past life I used a Swam Blaster from Crystal Mark with the media from them as well. I used it on Humiseal 1A31 and 1B31 (I think those were the products, it's been a little while). This machine and material were awesome IMO. Made CC removal a
Electronics Forum | Sun Dec 26 23:48:01 EST 2010 | raghu
Dear Sir, We are using 1B31 conformal caoting of 48 sec viscosity in Zahn #1 cup, by machine(PVA354) application with Tank air pressure 2.3 psi, automising air pressure 1 psi. 7 days after application we are observing peeling off problem.. And n
Electronics Forum | Mon Jan 03 00:30:30 EST 2011 | raghu
Contact your distributor for the coating or > Humiseal directly. Humiseal has had a recent > issue with batches of 1B31. The specific problem > is lack of adhesion, which is what you have as > well. You need to find out if your batch # is one >
Electronics Forum | Fri Dec 18 09:27:51 EST 2009 | sforman1
Tom: Once again - why are you using solvent based conformal coating. 1B31 is OK as a CC but it contains Toluene and MEK!! It is only 35% solids which means you are trying to get rid of 65% solvent. If you must use it due to customers requirement then
Electronics Forum | Wed Oct 17 02:04:39 EDT 2018 | robl
SCC3 has an operating temperature of 200C, as long as it is heat cured at 100C. https://www.electrolube.com/pdf/tds/044/DCA.pdf It's also a silicone so needs to be coated & cured away from anything you value. Otherwise there are plenty of PU's and
Electronics Forum | Fri Dec 18 09:07:24 EST 2009 | tommyg_fla
dave, where I work they are having the same problems with 1B31 acrylic. The coating thickness is 6-8 mils dried so that have to do several passes with an air dry between them and a final oven cure. They think that it might be related to the heating r