Electronics Forum | Sun Aug 10 03:41:20 EDT 2008 | eyalg
Thanks for your promt reply It was very usefull Eyal
Electronics Forum | Fri Aug 08 09:49:17 EDT 2008 | scottp
We've seen the exact same problem. The solder joints had negative wetting angles and x-sections show that the PdAg termination dissolved into the solder. We no longer allow PdAg terminations.
Electronics Forum | Sun Aug 10 03:39:21 EDT 2008 | eyalg
Thanks Pete yes we usu ROHS solder paste in our process. I agree that this termination is more suitable for adhsive bonding rather than soldering. We'll try changing the termination type as you recommended. Eyal G
Electronics Forum | Thu Aug 07 10:02:10 EDT 2008 | eyalg
We are facing low quality due to soldering opens with coilcraft inductors 0402CS-2N7XGLW. The termination used is(suffix L =RoHS compliant silver-palladium-platinum-glass frit. Did anyone had this problem in the past? Can we do better using T = RoH
Electronics Forum | Thu Aug 07 11:58:36 EDT 2008 | pbarton
We have experienced the same problem with Pd/AG and P/Ag terminations on precision resistive parts. The problem is dissolution of the termination metallisation into the bulk solder. This is exacerbated by the higher thermal profiles required for RoHS
Electronics Forum | Thu Feb 16 12:07:19 EST 2006 | dpmilk
We have been using Coilcraft 1008CS inductors for several years. We have had problems with them turning green when we use lead-free solder paste. We have tried several solder pastes (water soluble and no-clean)from different manufacturers, but the
Electronics Forum | Mon Feb 20 08:25:13 EST 2006 | Rob
No problem. If you get no joy you're going to have to change the footprint to a 1206 or 1210. Murata have a range of high Q value inductors (50-60) & from memory Toko used to be pretty hot too. The terminations on the coilcraft part are listed a
Electronics Forum | Mon Feb 20 09:20:07 EST 2006 | dpmilk
It appears to us that the problem lies in the lead-free solder paste rather than the inductors. We have not found a lead-free solder that does not do this. The green is on the copper wire. We believe it gets there during the reflow. The gasses fr
Electronics Forum | Thu Feb 16 16:16:19 EST 2006 | fredc
We saw something like this in the machine shop years ago. Fumes from a soldering operation in the shop turned exposed iron and steel tools and the spindle on my Bridgport mill green. Can your supplier apply plating or a coating to the exposed parts o
Electronics Forum | Mon Feb 20 07:59:50 EST 2006 | dpmilk
We saw something like this in the machine shop > years ago. Fumes from a soldering operation in > the shop turned exposed iron and steel tools and > the spindle on my Bridgport mill green. Can your > supplier apply plating or a coating to the >
winsouce.jpg)