Electronics Forum | Tue Jan 31 13:20:15 EST 2006 | mgdrouin1
Does anyone have any information regarding damaged caused to components due to overheating primarily with a heatgun? I'm having a hard time getting engineering to comply. Thanks
Electronics Forum | Tue Jan 31 13:22:15 EST 2006 | mgdrouin1
Does anyone have any information regarding damaged caused to components due to overheating primarily with a heatgun? I'm having a hard time getting engineering to comply. Thanks
Electronics Forum | Tue Jan 31 13:41:12 EST 2006 | outgasser
We are currently experiencing problems with delamination during rework/2nd op activity on lead free. I am suspecting this is a result of the use of a heat gun to rework components. My assumption is that the high heat and time in area greatly increa
Electronics Forum | Tue Jan 31 14:14:03 EST 2006 | samir
Ah, yes. The age-old battle of Production Supervision versus Process Engineering. I guess you just need to tell your Process Engineer, "Pretty please with sugar on top, investigate this f*cking issue."
Electronics Forum | Wed Feb 01 08:18:28 EST 2006 | slaine
RS sell a heat cun that is fully temperature adjustable buy one of them and pre set it to the right temp then put a calibration sticker over the control.
Electronics Forum | Tue Jan 31 14:30:38 EST 2006 | Chunks
There is none, since we don't know your part or temp being used. A heat gun CAN be used to remove parts with no damage, if its controled. You need to look up your part on the manufacturers web site, find the process data (time/temp)the part is desi
Electronics Forum | Tue Jan 31 14:58:15 EST 2006 | samir
You see? Chunks, here has the right idea! To the original poster, you need to show this post to your "Desk Jockey" Process Engineer. That's the problem with some Engineers today. They forget everything they learned in Engineering school, they get
Electronics Forum | Tue Jan 31 15:40:44 EST 2006 | mgdrouin1
Comp is relay. I've pulled the spec. Max 240. Using Leister h/g with manual temp settings from 1-6 (20 - 600C)set by the operator. Gun was set to setting 4. They are using the heat gun to reflow the solder after SMT but before wave. High fai
Electronics Forum | Wed Feb 01 22:27:16 EST 2006 | KEN
Many relays use soldered post coil terminatins inside the relay. In one case many years ago I found the SMT relay manufacturer used eutectic solder inside their hermetic relay. The SMT relay would fail because the solder balled up on the post, woul
Electronics Forum | Tue Jan 31 15:15:13 EST 2006 | russ
Heat guns used improperly will definitely damage components. You must have a controlled heat gun that can be set to the max temp you want pb =215C max, Pbfree maybe 240C max. This heat gun must not be able to be adjusted or you must have total trus
winsouce.jpg)