Electronics Forum | Tue Aug 15 07:02:13 EDT 2000 | George Verboven
We are assembling SMD-Leds (Chip LED cl-220yg-c-ts)on flex foil with Electrical conductive glue (Matthey A1401). When we investigated these foils we found cracks between the conductive adhesive and round the edge of the Chip-leds. This cracks cause f
Electronics Forum | Mon Aug 21 20:31:49 EDT 2000 | Dave F
George: I�d like to help, but I�m sorry I�m not familiar with your Matthey adhesive, can�t find information about it on the web, and can not picture the problem you are describing. Please post a picture and give us more detail. At least give us a
Electronics Forum | Thu Feb 24 08:29:01 EST 2005 | davef
We have done some work with conductive adhesives. The main lesson is: They do not adhere well to solder. * For components, a silver-palladium or gold end termination is recommended. * For substrates, gold over nickel should work well.
Electronics Forum | Wed Feb 23 09:33:03 EST 2005 | rlackey
Hi, Does anyone have any experience of using electrically conductive adhesives, including info on the following? 1) Autodispensing/screen printing 2) Curing temps/profiles 3) Quality/conductivity of joint 4) Product recommendations Our customer w
Electronics Forum | Thu Feb 24 06:41:14 EST 2005 | Rob
Hi Indy, Thanks very much for the info - very helpful. Was there any particular adhesive that stood out? Cheers, Rob.
Electronics Forum | Wed Mar 02 11:57:10 EST 2005 | Rob
Hi Dave, Thanks for the info, it will be helpful. Planning on trying it on a number of finishes, and have arranged for some samples of the adhesive - Loctite 3880 to start with. Have discovered something important already though - why not many peo
Electronics Forum | Wed Feb 23 10:36:37 EST 2005 | Indy
Hi Rob, I had tried printig anisotropic conductive adhesive as a replacement for solder paste. Following were my finding. Adv: - curing temp is around 120-150C as compared to 217C (Pb-free) solder. - good electrical conductivity, since it is usual
Electronics Forum | Mon Feb 28 08:06:49 EST 2005 | davef
You'll be able to tell pretty soon if this will work. * Our bet is the epoxy will corrode the silver. * Another concern is that you're not fusing the silver to the copper. Why not ask the imm silver suppliers: * Alpha Level Silver [ http://www.al
Electronics Forum | Thu Feb 24 10:34:02 EST 2005 | Rob
Thanks Dave, From what I remember a lot of components went away from Silver Palladium to "base metal" terminations because of the difficulties in continuation of supply & stability of price. (Something about being mined in Chechnia or the Congo?) W
Electronics Forum | Mon Feb 28 04:10:07 EST 2005 | Rob
Hi Dave, Was planning on skipping the paste step & screen printing the adhesive straight onto the pad, then placing the component into the glue & curing. (Board has LEDs only) Regarding the lead-free HASL issue - not entirely sure on the board man