Electronics Forum | Fri Jun 05 10:24:56 EDT 1998 | Earl Moon
| I have just been assigned to look into the ionic chromotograhy test on our PCBA but I have zero knowledge. Could anyone help to explain what is this test about? Is it | a) a destructive test? | b) What is the measurement unit of this test? | c) Wh
Electronics Forum | Mon Aug 24 08:44:52 EDT 1998 | Justin Medernach
| | | Require a conductive adhesive - either isotropic or anisotrpic - which can be used for 100micron oitch devices. | | | Must be resistant to solvents such as MEK and acetone. | | | Cure below 150C, with possible potential for rework of the conec
Electronics Forum | Mon Aug 27 10:58:44 EDT 2001 | Ryan Jennens
Steve- We had the same trouble with 0805 Panasonic film caps. We had some tombstoning and open solder joints (non-wetting). We found two problems...like you, we changed our pad design to meet their recommendation. Also, they were able to suppl
Electronics Forum | Wed Mar 04 11:16:25 EST 2009 | patrickbruneel
From your description of the problem first reduced SIR to dead short is exactly what happens with dendrite growth. What is needed to form them is low bias voltage (10 volt range is ideal with low current), a surface, 2 conductors (containing tin), io
Electronics Forum | Tue Oct 05 04:23:38 EDT 1999 | Brian
| | | | Can someone suggest what material I have to use to protect components by electrical discharge on ptfe based boards? | | | | It should have high resistivity, thermal stability (-40 +70 'C),perfect adherence on ptfe... | | | | Many tahnks | |
Electronics Forum | Tue Dec 14 22:17:33 EST 1999 | Dave F
Armin: How ya doin� bud? CK gives good advice, but I'd like to take a bit of a different angle. Q1. For 0.7 mm (0.027in) diameter hole for vias, what�s the minimum annular ring for this hole diameter? Depends on what you�re trying to do. For in
Electronics Forum | Fri Feb 25 02:30:32 EST 2011 | pkannan
Dstadem, Thanks for bringing your in valuable experience with the J STD 005 " Requirements of Solder Paste". I fully agree with you that the Solder Paste can be qualified for shelf life by doing simple viscosity test and visual inspection for coal
Electronics Forum | Thu Nov 13 17:18:11 EST 2003 | davef
First, don�t get distracted by �OA� and �NC� formulations. This is nomenclature. We want to discuss the issue of �activity�. J-STD-004 "Requirements for Soldering Fluxes" classifies fluxes by their chemical composition, activity level and halide c
Electronics Forum | Tue Sep 21 13:10:10 EDT 1999 | Dave F
| Dear All, | | In order to understand the soldering technologies in SMT, I'd like to understand why some cards are soldered and then cleaned, or only soldered whitout water cleaning nor "ultra sound" wavelength. | | I mean that I wonder why we use
Electronics Forum | Sun Aug 08 04:36:02 EDT 1999 | Brian
Dave Frankly, I think you may be barking up the wrong tree. Like DaveF, I suggest that the process would be horrendously expensive with masking and so on. The $64,000 question is whether what you propose will serve any useful purpose. I venture to