Electronics Forum | Mon Nov 08 13:38:37 EST 2004 | davef
You need to cover the chipped areas with a protectant coating, like epoxy. Look here:http://www.circuittechctr.com/products/115-1322.shtml We have no relationship, nor receive benefit from the company referenced above.
Electronics Forum | Mon Aug 01 18:50:46 EDT 2005 | crishan
Hi Cecil, We using conformal coating in our manufacturing area, we did use to use Humiseal, others have been Bectron and Peters. We recentalt switched all lacquering to Peters, since it is lead free and it is a lot friendly than Humiseal. To answer
Electronics Forum | Tue Jan 30 20:38:32 EST 2007 | davef
NASA Internal Advisory: NASA-Issued Return to Flight Wristbands Contaminated with Silicone [snip] 10. PROBLEM DESCRIPTION: Recently we have been made aware of a silicone problem associated with the "Return to Flight" wristbands. These wristbands are
Electronics Forum | Wed Apr 19 16:43:05 EDT 2006 | samir
Silicone-based coatings "repel" most foreign,non-compatible materials like peelable solder mask, and rubber or vinyl boots. The result is, uncured material around the vicinity of where the boot was. Trust me. Been there and done that. As a rookie
Electronics Forum | Wed Oct 03 17:07:52 EDT 2001 | davef
We have had soldering problems with fine pitch QFP in the past [and probably will in the future]. Several questions leap to mind: * When you took your profile on the component pads, do you profile on the pads that did not solder well? * When you say
Electronics Forum | Tue Sep 22 08:44:45 EDT 2009 | edmneb
It has stopped all together. We did go thru and touch up the solder joints. It says it fails to initialize the CRT.
Electronics Forum | Fri Oct 22 18:57:25 EDT 2010 | jry74
I am having a horrible time with the square radial lead capacitors (thru hole components) and the part coating flowing into the solder joint. These are Class 3 products. When we run them through the wave solder machine, the solder travels up the le
Electronics Forum | Mon Dec 13 21:11:53 EST 1999 | Curtis T.
Steve, I have done countless board profiling and oven reflow profiles. Here are the critical factors on you need to address. What is your board surface finish, if it is something like an OSP it will need a good amount of an active (aqueous) flux to
Electronics Forum | Tue Nov 24 05:23:18 EST 2009 | prodivegsr
Hi Davef, Thanks...Saw 1 of your thread that you posted : Thanks for providing... From davef : There are many possibilities: * Conformal coat is incompatible with surface residue on the board * Conformal coat is incompatible with solder mask on the
Electronics Forum | Wed Nov 25 15:16:04 EST 2009 | sforman1
Why in heavens name are you using a heat or air cure conformal coating. Why aren't you using a 100% solids UV cure system. You would never have an issue like this Sam Forman MicroCoat Technologies