Electronics Forum | Sun Apr 10 03:25:35 EDT 2005 | Peter
Normally, some conformal coatings do not have very good wetting properties, that should be basic function of a good coating material (the same reqirement as avoid bubbles during coating process)! For UV curing conformal coatings, you can try Lackwe
Electronics Forum | Wed Jan 27 09:00:56 EST 1999 | Chris Fontaine
| | I have boards coated with Humiseal 1B73. At a late point mfg. site we need to remove a series of 0603 resistors for optioning purposes. I have been trying to determine the fastest, easiest way to re-coat the pads after removal. Drying time of the
Electronics Forum | Fri Apr 21 17:46:29 EDT 2006 | SD
First of all, do not use kapton tape! It tends to cause a dewetting effect around the tape. A call to Humiseal will explain why. There's not really a blanket answer to your question.... Removing cured liquid mask can often result in a fillet ef
Electronics Forum | Mon Mar 11 07:05:06 EDT 2024 | klauss
while conveyor goes down to relaese pcb, some big compoments are swinging left or right due to high down speed of the conveyor. is there any way to decrease the speed?
Electronics Forum | Wed Dec 02 14:54:52 EST 2009 | jdumont
Hi all, just wondering what type of brushes you all are using to manually touch up/apply your conformal coatings? We use an solvent based acrylic and do minor touch ups as they are processed. Occasionally we will have a bristle or two come off the
Electronics Forum | Thu Dec 03 07:09:59 EST 2009 | jdumont
We spray with an Asymtek C-740 system. However, some very small PCBs we do by hand and we also touch up after a PCB has to be repaired.
Electronics Forum | Wed Mar 27 18:23:01 EST 2002 | kmorris
Does anyone have experience doing conformal coating over Plastic BGA in High-Rel PCB assembly? Is underfill necessary to avoid problems with entrapped air, etc? Our application is a 17x17mm BGA, 256 I/O. We are assembling with a water soluable pas
Electronics Forum | Mon Sep 21 20:45:55 EDT 2009 | davef
10.4. Pre-Cure Examination. Immediately after material application, the uncured conformal coating shall be examined for: a. Bubbles and Air Entrapments. These defects shall be broken by vacuum, with a sharp probe, or other appropriate tools. b. Bridg
Electronics Forum | Thu Aug 05 06:58:04 EDT 1999 | Graham Naisbitt
| | | Has anyone out there tried to parylene coat plastic parts prior to soldering them to a pcb? I'm looking at several potential applications where fewer than 5% of my components on a pcb are plastic, yet from a reliability aspect (environmental co
Electronics Forum | Wed Jul 22 00:43:05 EDT 1998 | P.L. Sorenson - Technical Consultant
| Who knows something about the reliability of plasti PEMS and its enhancemant by application of conformal coating (Parylene, metal, SiO2, SiNxOx, etc.) ? My personal experience using PEM for military avionics applications has been very positive. H
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
winsouce.jpg)