Electronics Forum | Tue Jun 02 15:53:32 EDT 1998 | Earl Moon
| We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not al
Electronics Forum | Wed Jun 03 07:13:27 EDT 1998 | Tom Tellinghuisen
| We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not al
Electronics Forum | Tue Jun 02 17:36:43 EDT 1998 | Chris Fontaine
| | We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not
Electronics Forum | Wed Jun 03 15:22:12 EDT 1998 | Greg Curler
| | We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not
Electronics Forum | Tue Jun 02 18:01:47 EDT 1998 | Earl Moon
| | | We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is no
Electronics Forum | Wed Jun 03 01:06:13 EDT 1998 | Mike Moninger
| We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not al
Electronics Forum | Fri Apr 21 17:46:29 EDT 2006 | SD
First of all, do not use kapton tape! It tends to cause a dewetting effect around the tape. A call to Humiseal will explain why. There's not really a blanket answer to your question.... Removing cured liquid mask can often result in a fillet ef
Electronics Forum | Fri Jan 05 12:01:26 EST 2001 | Jim M
I've been involved with no-clean flux and conformal coat in the past.It has been my experience that the amount of no-clean flux used is proportionate to how well the conformal coat adheres to the boards.No clean paste did not affect adhesion. The co
Electronics Forum | Thu May 26 16:41:00 EDT 2011 | scottp
Here's what I do: - Test Surface Insulation Resistance (we're in the high reliability market and use a test significantly harder than IPC's). I also test SIR in combination with other assembly materials like conformal coatings and wave solder flux
Electronics Forum | Sun Aug 13 00:15:58 EDT 2017 | deanm
We manufacture low volume, high reliability assemblies (class 3) that are conformal coated. Up until now we have been cleaning after SMT, then after through hole, then immediately prior to coating with test, formal inspection, etc. between cleaning p