Electronics Forum | Thu May 05 12:31:27 EDT 2005 | russ
Not in this case, these BGAs were lead free and the profile used was for a lead part. I guess I will give you the whole story. These boards were sent to us from a customer to have the BGAs replaced for an unknown to us reason. We removed the parts
Electronics Forum | Fri Sep 17 09:54:40 EDT 1999 | Brian
| | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a
Electronics Forum | Fri Sep 17 10:09:17 EDT 1999 | Earl Moon
| | | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However,
Electronics Forum | Sat Sep 18 12:27:21 EDT 1999 | Earl Moon
| | | Dave, I'll respond by paragraph: | | | | | Brian: | | | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like habanero slathered shiitake
Electronics Forum | Sat Sep 18 13:05:57 EDT 1999 | Brian
| | | | | | Dave, I'll respond by paragraph: | | | | | | | Brian: | | | | | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like habanero slath
Electronics Forum | Sat Sep 18 14:37:00 EDT 1999 | Earl Moon
| | | | | | | | | Dave, I'll respond by paragraph: | | | | | | | | | Brian: | | | | | | | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like
Electronics Forum | Mon Jun 12 07:42:56 EDT 2006 | brian.perry@suntroncorp.com
We are placing a gold plated device (LCC) to a NiAu PCB using a SnPb No-clean solder. We're noticing quite a bit of difficulty with reliable joints (intermittent connectivity) and if we have to rework a particular device, adjacent devices of this sa
Electronics Forum | Fri Sep 17 06:01:12 EDT 1999 | Earl Moon
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
Electronics Forum | Fri Sep 17 15:01:05 EDT 1999 | Dave F
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
Electronics Forum | Sat Sep 18 04:42:52 EDT 1999 | Brian
Dave, I'll respond by paragraph: | | | Brian: | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like habanero slathered shiitake burritos through
IPC is the trade association for the printed wiring board and electronics assembly industries.
Training Provider / Events Organizer / Association / Non-Profit
3000 Lakeside Drive, 309 S
Bannockburn, IL USA
Phone: 847-615-7100