Electronics Forum | Wed May 20 20:16:29 EDT 1998 | D. Lange
| We notice that DI water seems to tarnish or discolor the metal packaging on crystals and DIN connectors. Our marketing types like the shiney metal surfaces. We don't want to hand solder these parts after washing. | Any suggestions? | Dave F Dave,
Electronics Forum | Mon Dec 24 01:43:34 EST 2001 | sanmatech
Recently started running flex board with tin lead connectors. The problem being that when we receive the parts incoming connectors are all bright and shiny. Now after going thru the heller we encountered cold solder. At this time peak temp was at 186
Electronics Forum | Mon Jun 24 18:45:06 EDT 2002 | jersbo
I have done experiments on small runs, with a few connectors and have had favorable results, I had apertures (oversized)made for the thru-hole connectors on our SMT stencil and hand inserted the connectors.. A few insufficient solders here and there
Electronics Forum | Thu Jul 31 11:33:51 EDT 2003 | yngwie
I faced problem over connecter's pin that were hot air soldered. This connector has 168 pins ( similar to the straddle connector ). The process is to apply the flux onto the connector's J-leads, and the hot air pencil were then ran thru' the leads to
Electronics Forum | Mon Aug 30 16:07:06 EDT 2004 | Shean Dalton
Hi Chen, Based on your posted message, the following ideas are for your consideration: "brown residue" The water soluble solder paste you are using could be a water soluble rosin solder paste formulation. Perhaps the solder paste may not be proper
Electronics Forum | Wed Nov 03 14:46:29 EST 2004 | dramos1
Hi Russ, Thanks for the reply. In IPC-A-610 Rev. C on section 5.2.9 {Mounting - Connectors] page 5-21 on the manual [January 2000], the acceptable class [1,2,3]listed 3 items. In order for the connector to be accepted, are all 3 items must be met? I
Electronics Forum | Tue Jan 03 17:36:49 EST 2006 | MikeF
If you know you have cleaned any flux residues that were under there you could consider a bead of an electronic grade RTV, such as RTV3145. If you trap any uncleaned residues under there you could have long term reliability problems. But, like Dave
Electronics Forum | Tue Jun 13 04:20:21 EDT 2006 | Grant
Hi, ok, I have a bit more info after playing further with the profiling. We are getting close, but we don't have enough top side heat I think. The IR lamps just don't give enough, but we can get better connector that should help. But we have anoth
Electronics Forum | Mon Jan 15 01:13:25 EST 2007 | grantp
Hi, Does anyone know where to purchase the connectors? Specifically bulkhead connectors or PCB mount connectors. I am thinking about doing a general purpose SMEMA box that has a Basic Stamp in the core, and some buttons so I can use it for general
Electronics Forum | Sat Aug 11 05:29:31 EDT 2007 | johnz
We are having a problem with JST connector ICM-MA50H-SS52-1161 LF SN. After reflow oven soldering we have mostly problem with soldering quality for firs or last leg of the connector. (There is no connection- leg just lays-lift on the solder no wicki