Electronics Forum | Thu Oct 02 18:53:36 EDT 2003 | Michael Nguyen
We are using a Trek board washing system with 2 deionizer tanks hooked up to the 2 final rinse tanks and the first tank is directly connected with the city water. We are having problems with a vendor board on some tranformer/chokes. The part manufact
Electronics Forum | Mon Aug 27 15:06:29 EDT 2001 | davef
This otta push Wolfgang over the top ... Recommended reading G.G. Harman, Wire Bonding in Microelectronics : Materials, Processes, Reliability, and Yield, 2nd edition, McGraw-Hill Electronic Packaging and Interconnection Series, 1997. G.G. Harman, R
Electronics Forum | Thu Nov 03 07:43:52 EST 2005 | davef
Questions are: * Is the problem 'wire bonds that don't stick' or 'wire bonds that fall or break off later'? * What materials are you working with? * What is your working time after plasma clean? * What does surface analysis tell you about surface con
Electronics Forum | Thu Nov 03 02:34:46 EST 2005 | Rosewood
We've recently encountered some problems with wire bond strengths. I'm looking for anybody that has had some experience with different types of substrate contamination and methods for cleaning. There is no visible contamination on the gold pads, bu
Electronics Forum | Thu Nov 03 12:48:14 EST 2005 | Rosewood
We have some no sticks, but that is actually a good thing because we have NSD. During process control audits we found that pull strengths to the board dropped off. We build a military application that requires higher bond strenghts. Low pull streg
Electronics Forum | Thu Nov 03 21:40:40 EST 2005 | davef
There maybe multiple drivers to your problems. * First, decreasing bond quality with time indicates a plating issue. What's the actual thickness of your gold and nickel on the pads? * Second, the no-sticks indicate contamination. If it's organic, p
Electronics Forum | Thu Oct 05 16:04:00 EDT 2006 | GS
I am not expert, just my comment, the total ionic contamination allowed after SMT, by using No Clean process, theoretically it should be close to Zero. Any way the Standard IPC-JSTD-001 allows 1,56 ugr NaCl/cm2 for the final Printed Board assembled.
Electronics Forum | Thu Oct 05 07:23:34 EDT 2006 | Chris
Hi all experts, I have no background about PCB or SMT process. I am now encountering some issues after SMT - Unstable stitch bonding condition. I am now suspecting some contaminants remain on lead after cleaning. Therefore, how can I check th
Electronics Forum | Fri Oct 06 04:23:06 EDT 2006 | David
What is the solder finish of the board?. If this is gold, maybe you should check the reflow profile and max temperature which can easely kill your gold coating so problems with bonding. Also we are using Prozone Multicore with ultrasonic to clean
Electronics Forum | Mon Sep 09 15:38:02 EDT 2013 | arendonk
Hi, We are having issues aluminum wirebonding on ENEPIG plated PCB by a too low pull force and or having lifts (1% range). Could any body advice how to solve this problem? Is there a special wire bond grade required? How to best clean contaminant