Electronics Forum | Thu Aug 11 10:21:40 EDT 2005 | leonb
HI all, i have 2 omniflow 5 zone reflow ovens would these be suitable for rohs compliance also 2 iemme 760 reflow oven with 4 upper zone and 4 lower zones would these be suitable also any feed back would really help
Electronics Forum | Wed Dec 02 09:28:24 EST 1998 | Dave F
| Hi, | I'm looking for a small batch convection oven that will replace the dryer section of a batch ultrasonic cleaning machine to dry off excessive water from washed PCB's, | any suggestions for particular suppliers, will be appreciated. | Jack |
Electronics Forum | Tue Dec 28 10:04:01 EST 2004 | Mark
No delta T issues as I am not actually reflowing the component to the PCB. This is for moisture sensitivity testing as per JEDEC 020C Standard. Trying to duplicate a profile in the standard and am having trouble reaching a component ramp rate of 3
Electronics Forum | Mon Dec 27 18:44:14 EST 2004 | Mark
I am testing some BGA's (PBGA 30mm x 30mm) to evaluate the maximum ramp rate we can achieve in our reflow oven. Temperature is being measured at the body(top) of the component / not leads. After several trials (with various oven settings), the high
Electronics Forum | Mon Aug 16 20:19:10 EDT 2004 | Grant
Hi, We have both Vapor Phase ASSCON semi auto as well as Soltec convection inline ovens. I must say we had no end of problems with Vapor Phase. We tried everything, and just could not totally eliminate tomb-stoning completely. We would always get a
Electronics Forum | Thu Dec 14 04:42:11 EST 2017 | jineshjpr
Can anybody suggest how can I achieve good solderability in convectional reflow oven If I reduced Convection Air Speed 80%. The whole purpose is to reduce 0402 LED tilting in the convectional reflow and the PCB having QFN with 60 to 120 sec soak, 30
Electronics Forum | Thu Dec 14 05:07:55 EST 2017 | tsvetan
picture of the problem would help people to speculate what you do wrong
Electronics Forum | Thu Dec 14 15:05:17 EST 2017 | emeto
I am pretty sure, you are looking into the wrong spot. Your paste is too much, or your part has very inconsistent narrow leads(that includes wrong pad design as well.)
Electronics Forum | Wed Dec 20 07:16:16 EST 2017 | stephendo
I agree with Evtimov. What he didn't point out is that the surface tension of the solder would vastly overwhelm any force from air flow.
Electronics Forum | Tue Mar 16 17:14:05 EST 1999 | Matt Dussling
Looking for a company that makes a small batch reflow oven. Not a belt-style convection oven, but a cabinet style that can 125 c to 150 c. Thank you