Electronics Forum | Wed Jun 30 11:38:05 EDT 1999 | Brian Conner
| We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design). Ins
Electronics Forum | Wed Jun 30 12:14:40 EDT 1999 | John Thorup
| | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design). I
Electronics Forum | Thu Dec 16 16:28:51 EST 2004 | Indy
Hi, We are using Sn/3.0Ag/0.5Cu solder paste on Pd/Ag pad metallization in one of our application. Could someone provide me information on the following: 1. How bad is the Leaching of Ag in SAC alloy and how it can be mitigated. 2. During reflow so
Electronics Forum | Fri Jul 02 10:06:17 EDT 1999 | John Thorup
| | | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design)
Electronics Forum | Fri Jul 02 05:28:13 EDT 1999 | Vinesh gandhi
| | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design).
Electronics Forum | Fri Jul 02 09:54:02 EDT 1999 | John Thorup
| | | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design)
Electronics Forum | Fri Apr 10 18:51:39 EDT 2009 | boardhouse
Hi Jeff, Your board supplier could be correct in this way. The board could have had just a hair left of copper on the circuit, which would hold up under the electrical test process, but once you powered it up, then there was enough juice to burn th
Electronics Forum | Wed May 08 23:18:58 EDT 2002 | ianchan
Hi mates, have this SMT production issue : A) We have a leadless-chip-carrier(LCC) IC package that is classified under the Land-Grid-Array(LGA) package family. B) The LCC is 4mm x 4mm, and has 28 tin plated pads located beneath the outside perimet
Electronics Forum | Fri Apr 06 08:27:09 EDT 2001 | CAL
From what you are saying................If I hear ya correctly - There is no "Proctective" on the Pads (OSP, HASL....) You will be hard pressed soldering to bare copper. This can not be right. My suggestion- go polyimide with electroptical connecti
Electronics Forum | Fri Apr 06 08:28:34 EDT 2001 | CAL
From what you are saying................If I hear ya correctly - There is no "Protective" on the Pads (OSP, HASL....) You will be hard pressed soldering to bare copper. This can not be right. My suggestion- go polyamide with electroptical connectio