PCB oxidation

Electronics Forum | Wed Jun 08 13:49:48 EDT 2011 | sonofptolemy

Hello, I am having a problem with HASL PCB's after it comes back from the stuffer. To me it looks like oxidation and it causes poor wetting. This leads to a bunch of problems all of which have different symptoms but the cause is this oxidation proble

contamination on copper

Electronics Forum | Thu Apr 15 11:15:30 EDT 2004 | patrickbruneel

Pure (red) copper oxide is green, its not a residue its just oxidation. In your case water and heat will accelerate the oxidation process of unplated or unprotected pure copper. The best way to avoid this from happening is use a socket with tin or n

SMT fine picth connector lead oxidize-Throw out rate too high!

Electronics Forum | Thu Sep 05 22:01:55 EDT 2013 | davef

Questions are: * How did you determine that the coating on your component leads is oxidation? * What is the oxide? BR, davef

SMT fine picth connector lead oxidize-Throw out rate too high!

Electronics Forum | Wed Sep 04 22:48:13 EDT 2013 | winson16

SMT fine pitch connector having oxidation on lead and P&P machine keep rejecting the part. Is there any alternative way to reduce the part throw out rate without jeopardize the placement accuracy? Or is it possible to re-coat the connector lead or an

SMT fine picth connector lead oxidize-Throw out rate too high!

Electronics Forum | Fri Sep 06 14:03:18 EDT 2013 | horchak

If you are a CEM you are setting yourself up for failure and will be left holding the bag. Flash gold has one purpose. It is a protective coating for the base medal to keep it from oxidizing. It is very thin and will be absorbed into the solder joint

SMT fine picth connector lead oxidize-Throw out rate too high!

Electronics Forum | Fri Sep 06 07:40:02 EDT 2013 | spoiltforchoice

gold, one of the stablest elements on the periodic table oxidising. Are you sure, and why would you want to reduce the vision fail rate on a part that is clearly shockingly poor?

SMT fine picth connector lead oxidize-Throw out rate too high!

Electronics Forum | Thu Sep 05 23:32:29 EDT 2013 | winson16

This connector was designed with gold flash plating and the lead's surface was become dull and some black mark was observed on the contact surface.

SMT fine picth connector lead oxidize-Throw out rate too high!

Electronics Forum | Mon Sep 23 14:26:27 EDT 2013 | joekirin

On machines such as MyDatas you have the ability to mechanically center parts rather than optically centering. If your machine is capable of doing mechanical centering that would eliminate the need for the vision analysis. -Joe

SMT fine picth connector lead oxidize-Throw out rate too high!

Electronics Forum | Thu Sep 26 02:15:32 EDT 2013 | winson16

Thanks Joe. I will check through this with machine supplier to understand what's their machine's ability of doing this.

SMT fine picth connector lead oxidize-Throw out rate too high!

Electronics Forum | Tue Sep 24 04:14:25 EDT 2013 | winson16

Hi Joe, first of all thanks for your input. I did tried to search for the Mydata brochure and found that they are using Lifescan Vision System (LVS) which i think should be vision analysis. Appreciate if you can explain more in detail how's the mecha

  1 2 3 4 5 6 7 8 9 10 Next

copper oxidation rate searches for Companies, Equipment, Machines, Suppliers & Information

Thermal Interface Material Dispensing

World's Best Reflow Oven Customizable for Unique Applications
December 2024 Auction

We offer SMT Nozzles, feeders and spare parts globally. Find out more
Software for SMT

High Precision Fluid Dispensers