Electronics Forum | Fri Jan 30 00:41:04 EST 2015 | neeraj_iiser
Thanks a lot , my application is cryogenic in nature. I am trying to make a Sub-Angstrom resolution Thermal expansion sensor, whose components have been machined out of OHFC copper, and i needed to solder a manganin wire to one of the capcitor plates
Electronics Forum | Wed Nov 02 22:06:54 EST 2005 | davef
Slaine, our intuition is the same as yours [that 100Sn should dissolve the copper faster than other solders]. Bob Gilbert's FCT data shows otherwise. Look here: http://www.fctassembly.com/newsltr/2004/0804/Aug04.htm
Electronics Forum | Thu Jan 29 09:18:36 EST 2015 | davef
Nichrome, manganin, phosphor bronze etc are easy to solder ... the hard part is removing the corrosion * Manganin: 86% copper, 12% manganese, 2% nickel. Often, it's used in making cryogenic measurements, due to its low heat loss. * Select a flux for
Electronics Forum | Thu Nov 03 08:18:17 EST 2005 | fctassembly
Hello Arnold, Just to clarify the Sn100C discussion: Please note that SN100C is the Nihon Superior alloy composed of tin/.7copper/nickel. The key point in regard to SN100C is that Cu does not go directly into solution but first reacts to form an inte
Electronics Forum | Mon May 07 22:29:52 EDT 2001 | davef
4 wire per sec ... you figure how many you need] Encapsulation ~$120K for a dispenser [10 sec per die ... you figure how many you need] plus a cure oven ~$100k Throw in a another ~$100k for marking and cleaning Check the September 2000 SMTnet New
Electronics Forum | Thu May 18 03:15:32 EDT 2017 | wama
We are soldering wire 26AWG to jack socket. However after went through washing, baking, coating, curing processes the wire breaks (at joining point with jack socket) during wire dressing. We have tried to increase and decrease the solder amount but r
Electronics Forum | Wed Mar 04 10:24:50 EST 2015 | grenier
I'm looking for laser marking equipment for direct serial number Id on PCBAs. Is it recommended to laser mark on solder mask or copper or raw material?
Electronics Forum | Wed Mar 04 22:24:28 EST 2015 | SKR
We are using Nutek NTM4910-XL laser marker to etch 2D barcode on all our boards. We added solid silkscreen box on all our boards to create contrast. When we laser etch them, we just burn the silkscreen box so that we can see the soldermask under it c
Electronics Forum | Thu Dec 21 21:37:19 EST 2006 | Jack
Hi Pavel, Real Chunks, Thanks for your valuable inputs..Selecting the correct location for board profiling is critical in determining the solder joint quality. Am I right to say TC wire attachment locations priority should be as below: (1) Thermal
Electronics Forum | Wed Dec 20 23:29:32 EST 2006 | Jack
Hi all, Is there anyone know the correct way to obtain the accurate temperature profiling for oven reflow? Are below claims true? (1) Instead of full components on the PCBA (Motherboard), the profile taken from PCBA with few components can be cons