Electronics Forum | Sat Sep 08 08:55:24 EDT 2007 | davef
We expect to see a copper shadow along the edge of pads when soldering boards with organic solderability protection [OSP]. IPC-A-610 has defined this as acceptable for years. During early reflow stages, the flux in paste dissolves the OSP where ther
Electronics Forum | Tue Jun 30 11:12:19 EDT 1998 | Justin Medernach
| | | WHAT IS THE BEST ANGLE FOR THE SQUEEGEE BLADE TO BE ANGLED AT? WE ARE USING 45 DEGREE ON OUR POLYURETHANE BLADES, AND I BELIVE WE HAVE THE OPTION OF EITHER 45 OR 60 DEGREES ON OUR METAL BLADES. WHICH OF THE TWO IS BETTER, OR SHOULD WE BE USIN
Electronics Forum | Fri Jun 26 08:58:43 EDT 1998 | Justin Medernach
| WHAT IS THE BEST ANGLE FOR THE SQUEEGEE BLADE TO BE ANGLED AT? WE ARE USING 45 DEGREE ON OUR POLYURETHANE BLADES, AND I BELIVE WE HAVE THE OPTION OF EITHER 45 OR 60 DEGREES ON OUR METAL BLADES. WHICH OF THE TWO IS BETTER, OR SHOULD WE BE USING AN
Electronics Forum | Sat Jun 27 08:23:02 EDT 1998 | Dave F
| | WHAT IS THE BEST ANGLE FOR THE SQUEEGEE BLADE TO BE ANGLED AT? WE ARE USING 45 DEGREE ON OUR POLYURETHANE BLADES, AND I BELIVE WE HAVE THE OPTION OF EITHER 45 OR 60 DEGREES ON OUR METAL BLADES. WHICH OF THE TWO IS BETTER, OR SHOULD WE BE USING
Electronics Forum | Tue Oct 16 10:06:46 EDT 2012 | jackofallmasterofnone
Hello all, First off let me start by introducing myself. My name is Dan and I work for a contract manufacturer. During a job search I had heard from a previous co-worker that there was a packing job available at the facility where he now worked. I
Electronics Forum | Sat Jun 05 07:23:20 EDT 1999 | Dave F
| Where I can find some informations about repairing of SMT boards? | | Thanks | | Marcos | Marcos: Ya know, repair is that "dirty little" part of the business that all try to ignore, don't want to fund properly, and creats more angst than propa
Electronics Forum | Tue Dec 27 10:11:50 EST 2005 | pjc
Here's a few mfrs. to look at. http://www.vjelectronix.com/vjebeta/index.asp http://www.glenbrooktech.com/advantage.htm http://www.lixi.com/product_workstation.htm http://www.focalspot.com/ http://www.microfocus-x-ray.com/frameset.php?PageN
Electronics Forum | Tue Jan 23 09:03:00 EST 2001 | fmonette
This guideline is actually in the IPC/JEDEC standard J-STD-033, May 1999 (although it is not spelled out very clearly, thus the current confusion in the industry). The technical reason is that moisture diffusion is a very slow process. Once parts ha
Electronics Forum | Sat Jan 20 20:54:03 EST 2001 | fmonette
Dear Mike, As you might have noticed from the labels on the dry bags, the maximum floor life is specified by the component manufacturer and it can range from 1 year (level 2) down to a few hours after mandatory bake (level 6). This limit is based o
Electronics Forum | Sun Aug 08 04:36:02 EDT 1999 | Brian
Dave Frankly, I think you may be barking up the wrong tree. Like DaveF, I suggest that the process would be horrendously expensive with masking and so on. The $64,000 question is whether what you propose will serve any useful purpose. I venture to
IPC is the trade association for the printed wiring board and electronics assembly industries.
Training Provider / Events Organizer / Association / Non-Profit
3000 Lakeside Drive, 309 S
Bannockburn, IL USA
Phone: 847-615-7100