Electronics Forum | Thu Dec 07 10:10:49 EST 2006 | Learn from U
Hello, I need your advice..Welcome any input!! Cheers..
Electronics Forum | Thu Dec 07 14:23:30 EST 2006 | russ
I wuld say it is attachment method and post install force that is the problem not the size of the heatsink. we place heatsinks that are at least 5 times the size of BGA with no issue, they are attached with very precision torque drivers. Russ
Electronics Forum | Wed Nov 29 00:43:45 EST 2006 | callckq
Dear all, Recently, we run 2 models with heat sink attachment on top of this BGA(on top of this BGA, there is flip chip attached at the center of the BGA). Hence, the center of the BGA is higher than corner/side. We used conventional way to attach
Electronics Forum | Wed Nov 29 01:12:12 EST 2006 | callckq
Dear Davef, Thanks for your input...The crack happen at the pad/solder ball interface..Pls review the new thread that I post just now with title called "BGA BALL CRACK AT PAD/SOLDER BALL INTERFACE" Thanks!
Electronics Forum | Thu Jun 18 14:25:21 EDT 2020 | sara_pcb
We have observed Plastic BGA crack in encapsulation to substrate interface. After reflow, the device was not functioning. The Crack is observed in the fresh lot during visual inspection. What is the attachment process of package to substrate? where c
Electronics Forum | Sat Aug 22 05:19:42 EDT 2009 | ghepo
Dear Eric, in my opinion this is a very complex problem, that require to know many details for answer. For example : 1) what about the PCB finishing ? Have you verify the quality of they ? 2) what about the solder paste (the exactly composition)? 3)
Electronics Forum | Thu Jul 03 13:10:39 EDT 2003 | slthomas
I snapped a board in half at a cracked solder joint, and the component pulled free of the solder and still has a very thin layer of metal on the termination end. Based on the construction spec.(solder over nickel over palladium), it looks like it
Electronics Forum | Thu Sep 12 10:45:29 EDT 2002 | pbarton
We have used a laser cut stencil 0.15mm (0.006") thick with 0.3mm (0.012") square apertures radiused in the corners 0.06mm (0.0025") to aid paste release. This approach with the (type 3) paste we use has proven successful on thousands of devices plac
Electronics Forum | Tue Apr 07 13:17:10 EDT 2009 | tserra
I would recommend looking at SAKI/MacroScience. http://www.xraytechnology.eu/index.php?option=com_content&task=view&id=34&Itemid=42 I have seen the images created by MSX3000 from MacroScience which is now under SAKI and can tell you with certainty
Electronics Forum | Thu Jul 03 12:03:00 EDT 2003 | slthomas
So, there is a crack or gap between: * Solder and component termination. Bingo Correct? Describe: * Coarseness / smoothness of the metal on the termination underneither the crack. * Solder left on the termination. Unfortunately at 45X I can't rea