Electronics Forum | Wed Jan 15 10:31:55 EST 2020 | emeto
Having 10c thermal differential is a lot. Trying different paste might help - usually thermal expansion makes component detach from PCB, then joint is formed and solidified, then component goes back but is too late to form a joint. Cooling speed migh
Electronics Forum | Wed Jan 15 11:18:51 EST 2020 | avillaro2020
Hi Evtimov, Thanks again! The solder wicking/open solder joint is not actually gross rejection, it is only a few and appeared random (difficult to trend the location of the opens), what is perflexing is that i have this 1 or 2 open solder joints sur
Electronics Forum | Mon Jan 13 17:39:49 EST 2020 | avillaro2020
Hi, I need help on how to address the solder wicking on the samtec searay connector after reflow resulting to open solder joints on thick and thermal heavy PCB (4.4mm and 6.3mm). I increased my solder paste thickness to 8 mils, the connector is manua
Electronics Forum | Mon Feb 01 16:40:45 EST 1999 | Dave Waddick
I have a product using high temperature solder to connect terminal pins to a PCB. The board is single sided copper, no plaiting. The solder is 95% tin 5 % silver. The flux is low activity rosin. The product is a subassembly. When the product is
Electronics Forum | Tue Feb 02 12:31:26 EST 1999 | John
| I have a product using high temperature solder to connect terminal pins to a PCB. The board is single sided copper, no plaiting. The solder is 95% tin 5 % silver. The flux is low activity rosin. The product is a subassembly. When the product i
Electronics Forum | Mon Jun 28 11:47:54 EDT 1999 | Christopher Cross
| | | hello, | | | | | | has anyone tried dispensing solder paste in thru holes instead of waving or hand soldering. if so how did it work out for you. | | | thanks for the input | | | | | | wayne | | | | | | | | | | | We have tried this mainly
Electronics Forum | Tue May 23 22:23:20 EDT 2000 | JAK
Hi all, I'm would like to try intrusive reflow (pin in paste, paste in hole, etc.) on a connector using WS-609 solder paste (halide free, water-washable). I'm concerned about entrapped flux in the barrel of the solder joints. If there were to be e
Electronics Forum | Tue May 23 22:21:13 EDT 2000 | JAK
Hi all, I'm would like to try intrusive reflow (pin in paste, paste in hole, etc.) on a connector using WS-609 solder paste (halide free, water-washable). I'm concerned about entrapped flux in the barrel of the solder joints. If there were to be e
Electronics Forum | Thu Oct 08 22:32:58 EDT 1998 | Dave F
| | | | I am trying to find out, what possibilities I have, to print solder paste on a board, when the task is to have 120 Microns thickness for the biggest part of the board (85% of the real estate), and then have 250 Microns of thickness on the re
Electronics Forum | Thu Oct 08 03:27:00 EDT 1998 | Thomas Blesinger
| | | I am trying to find out, what possibilities I have, to print solder paste on a board, when the task is to have 120 Microns thickness for the biggest part of the board (85% of the real estate), and then have 250 Microns of thickness on the rema