Electronics Forum | Tue Nov 29 12:36:13 EST 2016 | kahrpr
If you are running a no clean process why are you cleaning
Electronics Forum | Tue Nov 29 19:15:41 EST 2016 | mowens
Thank you, I will see what I can find out.
Electronics Forum | Thu Dec 01 10:31:21 EST 2016 | sumote
Techspray Wonder Mask 2211
Electronics Forum | Tue Nov 22 15:21:54 EST 2016 | mowens
Is there some material that can be applied to a bluetooth module to keep wash water out. We need to clean the board, however, this part is not washable. We are running a NC process. Any Ideas?
Electronics Forum | Tue Nov 29 19:19:34 EST 2016 | mowens
Yeah, never made sense to me either, we have seen with this particular board variability in performance. I would like to apply a coating to keep the BT module dry and be able to wash the board then remove the coating over the module.
Electronics Forum | Tue Nov 29 08:03:29 EST 2016 | robl
Is it non washable or non ultrasonic washable? Just asking as there will be some sort of xtal in the module that may have harmonic issues. Worth checking with the manufacturer.
Electronics Forum | Thu Dec 23 12:32:57 EST 2004 | OverTheHill
All right all you Mydata techies. Here's the scoop. My old TP9 seems to be damaging (bending) it's A12 and A13 tools way too frequently. Like 4 tools in the last month. It appears the tool is colliding with somthing. My perfect operators SWEAR there
Electronics Forum | Tue Dec 11 15:31:53 EST 2007 | chrisatae
We accidentally mixed water wash with RMA flux. When the heat was applied during through hole soldering we noticed a problem and we cleaned it as soon as we discovered it. But now there's a discoloration where it was applied. Anyone experience this a
Electronics Forum | Fri Jul 28 12:13:38 EDT 2017 | dontfeedphils
Ironically enough, inline wash system belts work well for placing on top of small assemblies inside wash basket to avoid bouncing around like you've seen. This of course assumes you have access to an old belt like that. Point being, try to find som
Electronics Forum | Tue Jan 31 13:41:12 EST 2006 | outgasser
We are currently experiencing problems with delamination during rework/2nd op activity on lead free. I am suspecting this is a result of the use of a heat gun to rework components. My assumption is that the high heat and time in area greatly increa