Electronics Forum | Tue May 02 12:07:26 EDT 2006 | Sheldon Stewart (Process Engineer)
I am curious if everyone else is seeing the same dramatically reduced tip life with lead-free that I am? We have purchased new irones with controlled temperatures up to 800F. We are doing more hand soldering on our lead-free at the present while wait
Electronics Forum | Thu Mar 23 14:17:47 EST 2000 | Finepitch Services
Stuart, My suggestion is a DFM meeting (most of the process people dream about a meeting like this, and luckily, I've been to a few) with: - project manager (if there's one) - customer service rep (annual volume, lot size, product life) - smt proce
Electronics Forum | Thu Mar 23 14:17:47 EST 2000 | Finepitch Services
Stuart, My suggestion is a DFM meeting (most of the process people dream about a meeting like this, and luckily, I've been to a few) with: - project manager (if there's one) - customer service rep (annual volume, lot size, product life) - smt proce
Electronics Forum | Fri Dec 08 01:05:33 EST 2006 | Setup Guy
Hi Guru, I have a project to evaluate different kind of Solder Bar and Flux to be used in wave solder(RoSH)machine, to choose in which is the best to be use. What is your best practice to evaluate the Solder Bar and Flux ? Cheers, Setup Guy
Electronics Forum | Mon Dec 11 20:44:37 EST 2006 | davef
Title : LEAD-FREE WAVE SOLDER FLUX EVALUATION Author : Michael Havener Author Company : Benchmark Electronics, Inc Date : 09/25/2005 Conference : SMTA International Abstract : The European Union�s deadline to ban lead in electronic pr
Electronics Forum | Tue Nov 09 16:16:57 EST 1999 | Horace Johnson
We have a Ultra 2000 wave solder machine with a Lambda, Omega and Rotary chip waves. We are running three shift and our operators dedross the solder pot every 24 to 32 hours. That is skimming around the nozzles and pumps. Our maintenance does a compl
Electronics Forum | Sat Mar 06 22:26:34 EST 2004 | Ken
I think it is a good idea to "waste" money on this analysis. Especially if you phase in a SAC wave alloy. Silver is not toxicity free....and lead free waves can dross 3 to 5 times faster than SnPb alloys. This produces a greater potential for airb
Electronics Forum | Tue Jun 17 01:45:30 EDT 2003 | Dreamsniper
Hi, All these guys have provided you good solid infos already! All I can say is that check your wave solder machine's mechanical set-up too...and the Molten Solder Level in the bath must be maintained at an accurate level/height specially after ded
Electronics Forum | Tue Mar 03 09:29:48 EST 2015 | rgduval
A couple of things that have helped me with solder ball issues at wave in the past: 1. Flux. Insure good flux coverage on the bottom of the board. 2. Preheat. Insure that the board is sufficiently preheated for the wave operation. Since you're
Electronics Forum | Mon May 23 10:53:32 EDT 2005 | HOSS
Eric, We also have a UPK 650C. Our machine was configured for N2 and using the ConTour nozzle. If you're using this nozzle without N2 you're creating tons of dross unnecessarily not to mention probably getting tons of icicling. We found out the h