Electronics Forum | Thu May 18 19:45:32 EDT 2006 | grantp
Hi, The tin flush is a good idea, and better than the suppliers suggestion of filling with lead-free solder which is much more expensive. I guess we won't be leaving a KG of solder in the bath, but based on your experience, how much remaining sold
Electronics Forum | Thu Mar 17 03:07:17 EST 2005 | Chua
Hi, We are running lead free at wave solder now and the spray flux system is down. If we are going to able the flux manually, what problem will we be facing with the excess flux able. Appreciate for the advise.
Electronics Forum | Thu May 18 16:10:18 EDT 2006 | adlsmt
We did a tin bath on ours but it was provided for free by Nihon Superior so that is a no-brainer. It was better than taking a risk of having to dump the pot. If you cant get a free tin bath, then you should probably go ahead and fill it half way or s
Electronics Forum | Thu May 18 16:27:53 EDT 2006 | bman
I don't have any experinence with this, but my concern is that you are limiting the amount of contamination your pot can absorb before you ever run a board through. What I mean is that even if you are able to drain all but about a kg of the old sold
Electronics Forum | Thu Feb 28 16:17:14 EST 2013 | barryg
Hi All, after many years of talking about it we WILL be setting up a lead free line. What alloys and products would you recommend. We are seeting up a new wave machine here soon and could us some input.thanks
Electronics Forum | Fri Mar 01 17:39:58 EST 2013 | davef
The LF wave solder solder alloy that marketing-types of other LF wave solder alloys compare themselves to is Nihon Superior SN100C
Electronics Forum | Fri Aug 12 13:17:00 EDT 2005 | patrickbruneel
To all smt neters, In many different threads I have tried to bring awareness of the dangers lead free alloys pose to the reliability of solder connections. Many times those warnings have been waved by unscientific reports (from lead free solder manu
Electronics Forum | Fri Mar 14 05:38:42 EDT 2008 | meritajs
Hello Could somebody inform us about real consumption of lead free solder alloy SN100C on your wave solder process. We do not use some antiaxidant and had had alloy consumption about 1 kg per hour. What is your experiance? All sugestion will be well
Electronics Forum | Thu May 26 13:04:44 EDT 2005 | c111
Can anyone recomend tools for cleaning & adjusting of a lead free solder pot? I know it's not recomended to use the standard stainless tools. I was told by an FSE to use wood (kitchen) tools. Thanks
Electronics Forum | Fri May 27 14:21:27 EDT 2005 | Frank
Back in the day, we had a small solder pot used for dipping ICs that were freshly removed from defective boards. What tool did we use to clean the dross? A small piece of card board. After the card board got too toasted, we'd grab a new piece of c