Electronics Forum | Sun Mar 26 19:02:05 EST 2006 | ms
Hi We are running automatic stencil printers, open squeegees, stainless stencil, stainless blades, print speed 25-30mm/sec. We have a frustrating consistency issue printing .37x.3mm apertures on a 45pin LGA (11 pads each side, 1 large ground in mid
Electronics Forum | Tue Nov 21 19:23:15 EST 2006 | greg york
Had exactly the same problem the other week. Baked some boards did improve slightly but not convincingly. Washed bare PCb and found excessive HASL fluids left on board from improper rinsing and problem disapeared. Baking HASL fluid out is impossible
Electronics Forum | Wed Mar 12 08:03:30 EST 2003 | Surachai
Hi all Pls. help advise. Our board use RMA solder paste (Pb-free Sn96.5/Ag3.0/Cu0.5). Can we use No-clean paste flux (Delta 670S1) in rework process? If it can not be used, why?. Thanks very much for your advice. Surachai
Electronics Forum | Fri Feb 22 13:19:54 EST 2013 | caurbach
Our new Soltec Delta 3 has this feature (they call it mainwave pushup) where you can add up to 60 rpm to the pump after the leading edge passes over the wave. Unfortunately, our old Delta Wave doesn't have this feature. Ideally we'd like to set it
Electronics Forum | Mon Jan 15 13:31:11 EST 2007 | John S.
Since it is in a pallet, I would be sure the preheat temperature is correct across the entire assembly. We've seen large temperatue delta's across assemblies that are soldered in pallets. Could be overheated even or contact time too long. Interest
Electronics Forum | Tue Feb 07 11:26:40 EST 2006 | Cal Kolokoy
At the wave, you should collect data on the critical process parameters. The cliche being, it's better to control your process via SPC versus performing SPC on defect data. Perform a DoE to determine which variable interactions have the greatest eff
Electronics Forum | Tue Jul 13 14:19:00 EDT 1999 | JohnW
| | | Hi, | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants) | | | | | | Sec
Electronics Forum | Tue Jul 13 14:25:57 EDT 1999 | Earl Moon
| | | | Hi, | | | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants) | | | | |
Electronics Forum | Wed Jul 14 21:34:16 EDT 1999 | karlin
| | | | | Hi, | | | | | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants) | |
Electronics Forum | Thu Jul 15 14:38:38 EDT 1999 | JohnW
| | | | | | Hi, | | | | | | | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants)