Electronics Forum | Sat Jul 29 00:44:30 EDT 2000 | Jason
Thanks for all the ideas. I tried solder "thieves" by placing some desoldering wick behind the briging pins and it worked! I have yet to try Chrys' idea but I will first thing Monday. This is a new board that has had this problem from day one. I
Electronics Forum | Fri Jun 15 12:07:13 EDT 2018 | fern
My company is hooking up a delta max wave solder machine but we can seem to get the estop error to go away any one have a any experience with this issue.
Electronics Forum | Mon Dec 17 02:08:21 EST 2007 | mun4o
Hi, I have a lot of solder bridge in our wave soldering process.We use SACX0307 and Surf 11 flux.the SW mashine is Vitronics delta 6622.Itry to change flux and termoprofile but results is not god.Can you halp me - recommend me some flux or other adv
Electronics Forum | Thu Jan 13 10:24:35 EST 2005 | SuePH
The pallets are made of a black composite that is 5MM thick, and yes, the bottom is beveled to the cut out space for the connectors. The wave solder machine is a Treiber, so the wave height is hand set. I always aim for the center of the leading edg
Electronics Forum | Mon Dec 17 12:06:58 EST 2007 | pjc
5 Steps to Eliminate Bridges: 1. Establish (wave) Parallelism First and foremost, you must establish board-to-wave parallelism. This is the prerequisite to any wave solder process control. For an understanding of the power of this approach go to ht
Electronics Forum | Tue Jun 20 20:43:00 EDT 2000 | Dave F
Gary: Your flux supplier is the person for you to ask this question. For instance, the Lonco Superflo 26F that Jason was talking about last week has a preheat of 85�C to 110�C. * Thickness and number of layers of your board will affect you choice o
Electronics Forum | Mon May 14 13:56:54 EDT 2007 | jdumont
Agreed, I just bought a Electrovert Vectra Elite and have been very pleased with it thus far. I got the dual pot option for lead free changeovers and that has worked great. I can change pots in under 5 minutes, not counting the time to warm up.
Electronics Forum | Mon Feb 23 05:37:23 EST 2009 | emmanueldavid
Necoleta, PWB Blistering/De-lamination may not be due for Titanium finished threads / holders which is typically being used to draw high Shelf Life of Pallets and even flow across Auto Wave Soldering rails. There is also nothing to suspect on Liquid
Electronics Forum | Mon May 07 22:28:17 EDT 2007 | colormaker
radiant heat. 137c The hollis was a great machine. The one I had the prehead wass on or off there was no setting. The pot temperature guage was brocken so I had to guess and manually turn the heater on and off. The whole machine was covered with 1 i
Electronics Forum | Mon May 07 11:09:49 EDT 2007 | davef
4 Fluxer Operation 4.1 Set-Up and Check-Out the Fluxer 4.1.1 Spray Fluxer Set-Up and Check-Out 4.1.1.1 Pass a sample unsoldered board through the machine. 4.1.1.2 Remove the board just after passing through the fluxer and the air knife. 4.1.1.3