Electronics Forum | Wed Oct 17 14:52:25 EDT 2012 | rway
1) Is there something your design/pcb Engineer can do to lay the array out a little better for the wave (i.e. add substrates, board thickness)? 2)What do you mean by material movement? Single piece/continuous flow. 3) Shouldn't be too hard. You
Electronics Forum | Thu Oct 18 15:03:48 EDT 2012 | rway
2) Start with the PLC. What do the indicator lights tell you. Is your entry sensor working? Your PLC has status lights that should go on/off with the input/output conveyors. Can you be more specific about "not operational?" This is a broad stat
Electronics Forum | Thu Sep 16 21:46:16 EDT 2004 | jeremyt
I work for a major OEM as well, and we have close to 1000 stencils in house. We just recently went to a new way of labeling our stencils. We ordered metal ID tags out of McMaster, and assigned a Number to each stencil. We then attached each tag to t
Electronics Forum | Thu Aug 22 22:10:26 EDT 2002 | davef
Ooooow! �Can it be fixed?� Good question. How BAD did you damage it? * Since you are asking this question, I am NOT inspired by the potential that you have the skills to fix the board. Go Jeff Ferry�s site at Circuit Repair Center [If you can�t f
Electronics Forum | Wed Sep 29 12:51:55 EDT 1999 | Bob Barr
Never heard of the DRS-22C. I have had a DRS-22 for several years now. Purchased it when we started doing BGA's. The operators like it - good optics (split view), built like a tank, X-Y table easy to manipulate for alignment. I like it because I ca
Electronics Forum | Mon Feb 27 17:08:15 EST 2006 | GS
3,5 ugr/cm2 NaCl) or power components, or Raw PCB. Nothing with the solder process or fluxes. Ion Chromatography analysis was necessary to help understanding of contamination origin. When occasionally we run TIC on a NC assembled PBA (Paste ROL0 or
Electronics Forum | Wed Aug 19 08:00:55 EDT 1998 | Earl Moon
| Hi there, | I'm actually facing a lot of trouble with PCB's presenting up to 3mm of bow /twist at reception i.e. before assembly. The PCB size is 220 by 230mm. The boards are to be assembeled SMD double sides with 05.mm pitch on both sides. In orde
Electronics Forum | Wed May 29 02:35:46 EDT 2024 | hananana
Communication system plays a vital role in modern society, but the corresponding interference problem is also becoming increasingly serious, which brings great challenges to the stability and reliability of communication system. In order to improve t
Electronics Forum | Tue Jul 27 06:04:16 EDT 2004 | cyber_wolf
Grant, I know of a couple places that throw their paste out at the end of the day. I have worked in SMT for over 15 years and we have never thrown paste out unless it was contaminated, or dried out. We have never had a problem. If you ask me, I would
Electronics Forum | Fri May 12 07:53:40 EDT 2006 | egrice1
Sheldon, Tip life is directly related to temperature, IRON plating thickness on the tip, Alloy composition used and operator technique. High tin contents in lead free alloys attach the tips. Poor wetting and higher melting temperatures cause us