Electronics Forum | Fri Jul 19 12:31:18 EDT 2024 | mun4o
Hi all, we prepare a fully automatic production line from bare PCB to ready product in cartoon box. The steps in production are 1- smt, TH mounting and soldering, 2- conformal coating , 3 - depanelling / separate PCBs from panel / and etc. All machi
Electronics Forum | Wed Jul 02 02:46:44 EDT 2008 | tang
Hi Guys, I have few question would like to ask regarding pcb conformal coating: 1. Can I know which masking material is the best for easy apply, fast cure, fast & easy to remove after coating & baking. And no chemical reaction which will whiten the
Electronics Forum | Thu Jul 03 17:29:42 EDT 2008 | mikesewell
Re: item 3 - there are ultrasonic thickness machines (Panametrics makes one) that can measure coating dry with a small transducer head. A little pricey for ones that measure reliably in the .003" +/- .002" range.
Electronics Forum | Fri Aug 14 09:40:59 EDT 2015 | jvalverde
Hello, I want to make a simple conformal coating machine, I think in a Cartesian robot with MACH3 software. My questions are about the G-Code for the program (the software to design: % open/close nozzle, the paths (trajectory), import the pcb fi
Electronics Forum | Fri Jul 04 06:29:51 EDT 2008 | andrzej
Hi, 1. we use John C. Dolph company - AC-46 on production line. I dont get any benefits advertising this on forum (but I`d wish to ;) 2. we use stickers, or other hand made tools to cover areas from AC-46 - it depednds on need for project.
Electronics Forum | Wed Mar 04 10:59:24 EST 2015 | jpierre
Hi first DS65 version is a specific dilution for dispensing machine, in this case the typical process is following: application of the conformal coating extraction of solvent (low extraction power is better)2minutes and drying the drying can be done
Electronics Forum | Fri Feb 18 10:10:49 EST 2005 | Frank R.
Thanks Dave, The problem is on all 0805. Do you think it could be a reaction with the flux from the wave or the one in the paste. Do you think the problem is the viscosity of the coating. SPEC = Viscosity 150cP nominal ASTM D-1384. I ask you all
Electronics Forum | Sun Apr 10 03:25:35 EDT 2005 | Peter
Normally, some conformal coatings do not have very good wetting properties, that should be basic function of a good coating material (the same reqirement as avoid bubbles during coating process)! For UV curing conformal coatings, you can try Lackwe
Electronics Forum | Mon Apr 08 14:16:29 EDT 2019 | sever_83
We've never heard of seen of such a thing either. We tried a clean sample board and applied con coat. Same process through out and we saw nothing. After speaking with the original operators who was curing the boards he had left the boards much longer
Electronics Forum | Mon May 22 11:22:34 EDT 2000 | Pierre
Does anybody use a material which is repairable (removable chemically), low curing time (UV), masked areas cured, solventless, used with Nordson equipments ?
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
winsouce.jpg)