Electronics Forum | Fri Oct 13 17:21:05 EDT 2000 | Jason Nipper
A few weeks back we experienced a wave process problem where we received deposits on our pcb. At first we though it was dedrites but after an outside analysis of the deposits they were found to be tin. We have tried to remove the deposits with brus
Electronics Forum | Wed Apr 30 17:17:21 EDT 2003 | swagner
Since you mentioned voids I take it you are talking post reflow correct?
Electronics Forum | Wed Apr 30 18:38:22 EDT 2003 | Guillermo
Yes, I am sorry I forgot to mention that It's inspection after reflow.
Electronics Forum | Wed Apr 30 12:30:14 EDT 2003 | Guillermo
Hello, I would like to ask for cooments/advices about the inspection of small solder deposits inspection (aprox 4 mills). We tried with X ray and Scanning acoustic microscope but it looks like due to the small size, we could not be sure to get all t
Electronics Forum | Tue Oct 17 14:40:04 EDT 2000 | Glenn Robertson
Jason - I have only one thing to add to Dave's excellent (as usual) information. Some time back we had a similar problem and we removed the dross bits with a soldering iron and solder wick. Yes, it's tedious and you have to look closely to be
Electronics Forum | Mon Oct 16 20:29:32 EDT 2000 | Dave F
Jason: How did you determine that the deposits are tin oxide? What does this stuff look like? Klein Wassink "Soldering in Electronics" (p. 221, quoting original work by others). States (in effect) tin (or solder) quickly forms a protective oxide
Electronics Forum | Wed Oct 18 10:02:04 EDT 2000 | Jason Nipper
I know it's a tin residue because we have a Cheme in house who had a spectrum analysis performed in an outside lab. The waves parameters were out of control long enough to effect a number of units that are, we�ll can I say substaincial in a fiscal s
Electronics Forum | Mon Mar 05 17:16:11 EST 2001 | lileubie
Hello All, Does anyone have any experience with soldering to vapor deposited metallizations such as gold? Or, does anyone know of any papers discussing soldering to vapor deposited metals? Any info would be greatly appreciated. Thanks, Glenn
Electronics Forum | Mon Jan 06 23:25:29 EST 2003 | Dreamsniper
I made an experiment with our semi-auto stencil printer and used my naked eye to decide whether the alignment and deposition is pass or fail. I based the results in percentage and 100% is perfect result. Now here's the question: Can anyone tell me w
Electronics Forum | Wed Mar 11 17:51:22 EDT 2009 | GSx
Thank you so much Dave, by having different lots of PCB received (same Supllier) with suspected and good carbon ink deposit, I found useful to adopt a comparison test among the different lots by usingthe IPC-TM-650 2.4.1 Adhesion , Tape Testing (lik