Electronics Forum | Mon Jun 15 15:33:51 EDT 2009 | hegemon
IMHO I would suggest that if you are using flux only during a BGA placement on a small run, that you first tin the pads with your soldering iron, then level the pads back out with wick. Accomplishes two things; adds a little metal to the joint to ma
Electronics Forum | Mon Jun 01 21:40:18 EDT 2009 | kircchoffs
i need some inputs regarding this process. is this really eliminates voids and other solderability issues on BGA's?
Electronics Forum | Tue Jun 02 22:19:17 EDT 2009 | mikehe
We have been doing BGA's for years now, and I would suggest updating your profile and place a thermal couple on the BGA, keep in mind the bigger the part the more heat it will need, We stencil print all of BGA's from simple bga's to complex ones, you
Electronics Forum | Tue Aug 14 23:58:19 EDT 2001 | Glen Brian
We are using the new auto-dipping machine for LED solder dipping and dragging. The flux is water-soluble flux and the solder is 63/37 at 250 deg. C. Two weeks ago we exchanged the pot with new 63/37 solder. About a week, we found that the high level
Electronics Forum | Wed Aug 15 16:04:23 EDT 2001 | davef
First, responding to your question � Several things on copper dissolution in solder are: * A 50um copper wire will dissolve in 60Sn / 40Pb solder at: - 200�C solder in 55 seconds; - 250�C solder in 20 seconds; - 300�C solder in 5 seconds; - 350�C so
Electronics Forum | Tue Mar 20 20:14:40 EST 2001 | davef
Electroplating [electrolytic] and dipping [HASL] are the two methods for applying solder coatings to features on boards. Disadvantages of electroplating lead / tin are: * "Weak knees" created at the edge of plated through holes. [I used to get weak k
Electronics Forum | Wed May 03 11:39:44 EDT 2006 | Chunks
"and dip it in your solder bath for 10-20 seconds." Do you pre-tin them first or just dip them in regular solder? "You can't talk to molten solder, but surfactant will listen." "Remember, we're all in this together."
Electronics Forum | Thu Nov 17 03:34:51 EST 2005 | cangly
Hi, We have a board with over 100 chips (mixed size) and some long Connector DIP through out Wave solder with many issues of no solder and solder bridge, (using clean flux with bubble fluxer and Kester solder bar). Currently we tried to reduce the de
Electronics Forum | Thu Apr 17 17:38:57 EDT 2003 | Takfire
Dave, I am not exactly sure what is driving them to believe that this is a capacitor issue. It is unfortunate, that this belief has slowed their activity in further understanding their manufacturing process. The caps are BME (Base Metal Electrode
Electronics Forum | Wed May 03 11:12:08 EDT 2006 | samir
Iron huh? You sure about that? We have the ERSA Versaflows and our nozzles are made out of ST37 Tool Steel. There is an "American equivalent" to this grade but I forgot what it is. You'll have to google it like I did. Anywho, Tin or Tin-Lead sold