Electronics Forum | Thu Feb 13 16:23:07 EST 2020 | alvarez94
I checked it and there is no problem with the lubrication the cables are in good condition. The band feels a little loose I will try to make the adjustment to see if that is the problem.
Electronics Forum | Fri Oct 14 14:00:35 EDT 2005 | patrickbruneel
Mika, If I understand you correctly you compare hole fill of Ni/Au plated boards in a lead-free process with HASL 63/37 boards soldered with leaded solder. If this is the case you might be facing the challenges in Pb free wave soldering with the lim
Electronics Forum | Tue Oct 18 00:31:17 EDT 2005 | KEN
I suspect the problem is a surfactant issue in your flux. I have seen where boards are fluxed, hit the solder fountain and come out like they never touched the solder. There was an inadequate surfactant between the solder and the PCB. I know you
Electronics Forum | Wed Feb 12 15:11:29 EST 2020 | alvarez94
I was consulting the manual of the machine and to measure the tension of the x belt I need a frequency counter and two prisms but I don't have these tools, is there any other way to measure the tension?
Electronics Forum | Fri Oct 14 10:55:07 EDT 2005 | Mika
We have a simular problem with Ni/Au; especially whith pcb thickness more than 1.8mm. Note: These boards have been through reflow process also. 1.)Is there a maximum board thickness where it would be almost impossible to get a decent hole fil? 2.)Wi
Electronics Forum | Thu Oct 13 15:41:30 EDT 2005 | lyrtech
Hi, We have a customer who give us a 20K board contract each year. It's only thru-hole components.The baord is HASL plated. So we pass it into our wave. No problems. Recently, our customer decided to go into GOLD PLATED finish. We take the same re
Electronics Forum | Fri Oct 14 09:58:13 EDT 2005 | patrickbruneel
Here's what I believe is happening. The main difference between the HASL boards and the gold plated boards is that HASL boards are pre-soldered. HASL boards need very little flux activity to get good hole fill and the machine settings have a wide pro
Electronics Forum | Fri Oct 14 11:56:49 EDT 2005 | patrickbruneel
Mika, 1.) Is there a maximum board thickness where it would be almost impossible to get a decent hole fil? Answer: The thicker the board the further the solder has to travel and the more you depend on solderability of boards and components, machine
Electronics Forum | Sat May 29 16:56:26 EDT 1999 | Jeff Sanchez
| | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a double-
Electronics Forum | Sun May 30 10:15:34 EDT 1999 | Vic Lau
| | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a dou
.gif)