Electronics Forum | Tue Sep 10 14:43:21 EDT 2002 | finepitch
I'll keep this short and end with another CM sales pitch. I do not suggest "cutting the bleeding arm" as few others suggested. There are good CMs sending "fully" populated boards. And there are good overseas ones where their average wage is US$4 wh
Electronics Forum | Mon May 31 21:50:59 EDT 1999 | Dave F
| | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a double-
Electronics Forum | Sun May 30 18:52:35 EDT 1999 | Graham Naisbitt
| | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a
Electronics Forum | Mon May 31 15:09:56 EDT 1999 | JohnW
| | | | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processi
Electronics Forum | Mon May 31 15:10:14 EDT 1999 | JohnW
| | | | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processi
Electronics Forum | vsuresh |
Mon Apr 15 11:48:14 EDT 2024
Electronics Forum | Mon Apr 15 16:33:37 EDT 2024 | cyber_wolf
Unskip part npm1 or take npm 1 out pass thru mode
Electronics Forum | Tue Apr 16 20:38:03 EDT 2024 | digitalshovel
when in assign mode, set npm1 as pass. The condition set will make it pass through to npm2
Electronics Forum | Wed May 01 11:47:44 EDT 2024 | linux
Panasonic provide several courses beginners to advance. Not very expensive
Electronics Forum | Mon Oct 20 15:24:52 EDT 2008 | davef
During reflow soldering, sometimes via fill with solder leaving the solder connection starved. Questions are: * Specifically, what is the problem you see? * Do the defective pads show that solder has melted in a uniform fashion? * How do the tempera