Electronics Forum | Thu May 18 03:15:32 EDT 2017 | wama
We are soldering wire 26AWG to jack socket. However after went through washing, baking, coating, curing processes the wire breaks (at joining point with jack socket) during wire dressing. We have tried to increase and decrease the solder amount but r
Electronics Forum | Wed Dec 28 16:03:53 EST 2005 | Chris
I have lots of experience with thermosonic gold ball bonding. You can read the literature and you will probably find some papers that say you can do it. I have never been able to do it. We gold ball bond all day long with little problems at all bu
Electronics Forum | Thu Dec 29 03:57:16 EST 2005 | sparrow
Hello Chris, To be honest, it's hard to believe you could not bond to ENIG at all. Yes, the gold layer is thin and hard, but it just narrows the process window and does not make the bonding impossible. I say this, because we have been using TS gold w
Electronics Forum | Wed Mar 11 19:22:02 EDT 2020 | victorzubashev
Hi, 1. do not use flux-cored wire- the smell is bad and flux will evaporate anyway at the time of solder wire melting. 2. as suggested use solder bars, something like this: https://smtnet.com/company/index.cfm?fuseaction=view_company&company_id=39635
Electronics Forum | Fri Feb 28 14:53:08 EST 2020 | rlising
Hi, I purchase a leadfree aven solder pot 300w. We are wanting to pre tin power and ground wires prior to soldering onto pcb. I have some anti-erosion flux cored wire solder from koki S03x7Ca-70m 1.6mm. Can this solder be used? If not what is t
Electronics Forum | Mon Mar 02 11:15:23 EST 2020 | slthomas
You'll want to chop your solder into "bite sized" pieces for your pot, by the way. A bolt cutter or a band saw are a couple of ways to do it without ruining other precision tools. It's up to you for the alloy you use, but there are several (some
Electronics Forum | Thu Sep 04 21:50:47 EDT 2003 | davef
We like to use "enameled wire" that can be stripped by hot solder. Formvar [105�C] will not do that. Formvar was designed to with stand the hot oil seen in transformers. So, it requires either chemical or mechanical stripping. Most polyurethanes
Electronics Forum | Tue Apr 16 05:05:32 EDT 2013 | stivais
We recently had a discussion with customer's QM - he claims that calculations for a proper solder wire diameter and soldering iron tip size (and temperature) have to be performed and documented for all manual (T/H) solderings (based on component size
Electronics Forum | Thu Jan 23 23:00:42 EST 2014 | davef
I agree with AFlex. Don't tin stranded wire that's assembled into a screw terminal block. I believe the reasoning has to do with avoiding stress on the wire metal caused by different expansion rates of the solder and the wire. BR davef
Electronics Forum | Fri Aug 17 01:40:55 EDT 2001 | V.RAMANAND KINI
We are in the watch & clock Business. We have a Watch IC chip that has to be wirebonded using Ultrasonic aluminium wedge bonder. The wire dia is 1.25mil. The PCB is made of G10 Glass epoxy copper clad laminate. The copper thickness is 18 microns. The