Electronics Forum | Wed Feb 22 12:19:49 EST 2006 | Dirka Jihabi
I worked for a EMS who makes Medical Device Electronics, and yeah, the FDA's methodology for validation is a complete cluster-fudge! They did it on the principle of...does the shop air going into your equipment REALLY 80 PSI...or is there REALLY 220
Electronics Forum | Wed Mar 15 17:13:21 EST 2006 | Wave Master Larry
Listen.I posted this same message on a diffrent thread but got no repsonse. Here's what im wondering Im more of a wave guy but we had a good employee in the engineering department, he's left the company but he used these setpoints on the ovens in a
Electronics Forum | Thu Apr 27 05:22:51 EDT 2006 | slaine
we have a small batch oven. It is does take a long time to cool but we set up an airline that blows in the door when its open and that helped things a lot. looking at the hot plate your thinking about going with, it doesent look like you can program
Electronics Forum | Tue Oct 03 09:23:55 EDT 2006 | kenscj
We are encountering BGA solder open connection. At Functional Test, the board failed. Debug guy diagnosed this BGA open connection (2 locations), by using multimeter. Under 5DX inspection, there is connection. Take the board for localised reflow at
Electronics Forum | Fri Dec 01 06:31:53 EST 2006 | CHITRA K
We use SMBJ5.0A - D0214A package component in our products.During production recently we have identified a seroius problem. The problem is, After reflow soldering the impedance becomes more / lesser and due to which the product does not work since th
Electronics Forum | Fri Feb 09 08:07:41 EST 2007 | jax
Has the board been looked at under X-Ray? Have you built more than 1 of the boards in question? Do any of the other boards have the same problem? Have you made any changes to the profile between boards? One side of the BGA collapsing during reflow w
Electronics Forum | Wed Mar 21 10:00:13 EDT 2007 | slthomas
"Unfortunately breakaways aren't an option - they are large boards and we already have problems hand placing components and probing them." Not sure what this means in this context....if you frame the perimeter with a 1/2" border on a V-score, how do
Electronics Forum | Mon Dec 17 09:38:56 EST 2007 | dborgelt
We have an outdated Metcal rework station and are thinking about purchasing a new one. We need something that has heat profile capability. We don't really need anything automated, just something that's affordable, durable, and gets the job done. Does
Electronics Forum | Wed Apr 30 12:26:10 EDT 2008 | dphilbrick
There must be discussions about this on SMTnet but I have yet to find them. I would like to hear from all you smart people about running LF and PB BGA�s on the same board using 63/37 solder. If you run your profile up to peak at around 225C +/- (nitr
Electronics Forum | Thu Aug 28 21:43:23 EDT 2008 | davef
Couple of points: * We'll tell ya, although it's tough to tell from these pix, but it does not look like dewetting. It looks like nonwetting. * We don't think you're getting this product hot enough. We don't know where you measured the profile you po