Electronics Forum | Thu Jul 19 22:12:52 EDT 2001 | davef
We don't use the connector that is giving you soldering problems. Regardless, no one here is taking bets that you'll get pay-back from increasing the length of the locking pin. If it makes you feel any better, we'd bet against a 4-40 flat head and
Electronics Forum | Wed Dec 29 15:42:34 EST 1999 | Mike Naddra
Justin, I would be currious as to your customers application, and if the temperature delta and rate are great enough to cause solder joint failures as a function of mismatched Tce then you may want to consider that even if you are able to identify
Electronics Forum | Thu Nov 18 09:34:58 EST 1999 | Wolfgang Busko
Hi Will, it�s possible to use second reflow for second side components without glueing or use of different alloy solders. Although the first soldered joints become liquid during the second pass the parts will not fall off as long as their weight does
Electronics Forum | Tue Oct 05 03:49:04 EDT 1999 | Chris May
| Hi everyone, I need some help on the whole process of double sided surface mount. We have been doing surface mount for about 3 months and we're getting ready to take on our first doule sided board. I just need some step by step process regarding so
Electronics Forum | Mon Oct 04 11:28:46 EDT 1999 | Mark D.
Does anyone have a list of component types that can be put on the bottomside of a doublesided reflow board that will not fall off during the second pass (Or on the otherhand, a list of components that will fall off)? This would be a list of parts tha
Electronics Forum | Mon Oct 04 11:23:55 EDT 1999 | Mark D.
Does anyone have a list of component types that can be put on the bottomside of a doublesided reflow board that will not fall off during the second pass (Or on the otherhand, a list of components that will fall off)? This would be a list of parts tha
Electronics Forum | Mon May 03 09:42:45 EDT 1999 | Mike McMonagle
| Tombstoning 0805s w/palladium/platinum/silver terminations | | We are experiencing tombstoning problems on 0805 packages that have paladium/platinum/silver terminations. It comes & goes...... | | I�ve checked the reflow profile, and paste deposi
Electronics Forum | Mon Mar 01 11:03:51 EST 1999 | Dennis Xiong
Hello! SMT professionals, I do not know if anyone posted this question before. Last week, I reflowed our newly designed thin Rigid-Flex pcb with 0.040" thickness. I found all of pins of a TQFP48 ic did not get wetted. I could see on the heel side o
Electronics Forum | Mon Mar 01 11:03:22 EST 1999 | Dennis Xiong
Hello! SMT professionals, I do not know if anyone posted this question before. Last week, I reflowed our newly designed thin Rigid-Flex pcb with 0.040" thickness. I found all of pins of a TQFP48 ic did not get wetted. I could see on the heel side o
Electronics Forum | Wed Dec 09 14:36:26 EST 1998 | Earl Moon
| Hi, I know for sure that by controlling temp. and humidity | conditions in SMT assy lines room, one gets advantage in | screen printing, adhesive dispensing, and pick&place | machines mainteinance. Does any one have any advice on why | else is a c