Electronics Forum | Thu Aug 27 11:35:07 EDT 2009 | davef
There are many possibilities: * Conformal coat is incompatible with surface residue on the board * Conformal coat is incompatible with solder mask on the board * Moisture is out-gassing from the board * Conformal coat is too thick and does not allow
Electronics Forum | Fri Apr 21 17:46:29 EDT 2006 | SD
First of all, do not use kapton tape! It tends to cause a dewetting effect around the tape. A call to Humiseal will explain why. There's not really a blanket answer to your question.... Removing cured liquid mask can often result in a fillet ef
Electronics Forum | Tue Jul 28 17:35:07 EDT 1998 | Brian Stumm
Steve, I know it is tempting to go for the cheapest method of applying conformal coatings but I must warn you. If you are a contract manufacturer then you don't want to limit yourself in the types of coatings you can work with. Just as soon as you se
Electronics Forum | Tue Jul 28 17:44:03 EDT 1998 | Brian Stumm
| Steve, | I know it is tempting to go for the cheapest method of applying conformal coatings but I must warn you. If you are a contract manufacturer then you don't want to limit yourself in the types of coatings you can work with. Just as soon as yo
Electronics Forum | Fri Jul 24 13:04:55 EDT 1998 | Dave F
| Hey youse guyz... | We're finally getting our first real job at the start-up I'm working at. It's actually a pretty unique little board too. Simple as all get out, but unique. You're not gonna believe what this goes into...guess? (I bet ya' you'll
Electronics Forum | Wed Mar 04 10:23:03 EST 2015 | rgduval
I haven't used this particular CC, but...found this in their data sheet: "AVR 80 BA Conformal Coating will be touch dry after 15 - 20 minutes at room temperature and does not require a thermal cure. The full properties of the coating will be obtaine
Electronics Forum | Thu Mar 31 10:14:06 EST 2005 | davef
There's some nice low-VOC uV coatings out there. We don�t use uV cured coatings, but try: * http://www.emersoncuming.com * http://www.dymax.com * http://www.mgchemicals.com * http://www.loctite.com * http://www.humiseal.com Be aware that uV co
Electronics Forum | Fri Feb 18 15:27:38 EST 2005 | jluckenbaugh
Frank R, I believe the Dymax #984-LVUF is a POLYURETHANE RESIN. I have used Humiseal 1A27 and 1A33 for several years with great success. Both of these materials are High VOC materials. If your customer does not require these materials to be aproved
Electronics Forum | Fri Apr 22 10:12:14 EDT 2005 | davef
Common RTV does out-gas causing corrosion. NASA allows use of non/low-out-gassing RTV. Try the following companies: * Ablestik Electronic: Materials, 20021 Susana Road, Rancho Dominguez, California 90221 U.S.A., 310-764.4600, F 310-764-2545 * Arlon
Electronics Forum | Tue Nov 24 05:23:18 EST 2009 | prodivegsr
Hi Davef, Thanks...Saw 1 of your thread that you posted : Thanks for providing... From davef : There are many possibilities: * Conformal coat is incompatible with surface residue on the board * Conformal coat is incompatible with solder mask on the