Electronics Forum | Mon Jun 12 07:42:56 EDT 2006 | brian.perry@suntroncorp.com
We are placing a gold plated device (LCC) to a NiAu PCB using a SnPb No-clean solder. We're noticing quite a bit of difficulty with reliable joints (intermittent connectivity) and if we have to rework a particular device, adjacent devices of this sa
Electronics Forum | Tue Jun 13 08:17:06 EDT 2006 | davef
The solder alloy does not change based on the flux. Your potential for embrittlement is the same [providing the metal of the solders are the same] with either solder. We would guess the OA flux is [and drag tinning are] removing corrosion from the
Electronics Forum | Thu Apr 27 03:23:25 EDT 2006 | ge_lim
According to seho, for multi dipping the process window is very small and they would prefer drag soldering which has a wider window. What is your view on dip vs drag? Why? Other machine user also share the same suggestion?
Electronics Forum | Tue Dec 11 11:59:00 EST 2012 | sarason
The issue is surface tension around the connector. Your tip needs to have more surface tension than the pins of the connector as it forms a cluster when being soldered. When I used to solder superfine connectors with a metcal iron it had a horses hoa
Electronics Forum | Mon Nov 30 09:02:13 EST 1998 | Chrys
Drag the iron and molten solder over the thermocouple to the left, encapsulating the bead. Now, obviously if you are left-handed, reverse everything. This is a foolproof way to attach thermocouples. I used to have a lot more difficulty with them u
Electronics Forum | Fri May 19 13:40:36 EDT 2006 | grantp
Hi, Sorry to drag this thread up again, but we were recommended to change the wave to SAC305, but is everyone recommending SN100C? That seems to be the feeling on this thread. What flux is used? Regards, Grant
Electronics Forum | Thu Dec 06 12:37:14 EST 2012 | deanm
We are having difficulty with bridging on a 2x50 pin 0.050" fine pitch connector using our selective soldering machine. It usually bridges at the end of the row, but sometimes it bridges all the pins together as it drags across (solid bridging). I
Electronics Forum | Thu Jul 15 14:38:38 EDT 1999 | JohnW
| | | | | | Hi, | | | | | | | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants)
Electronics Forum | Thu May 21 22:20:18 EDT 1998 | Earl Moon
| I am a former employee of a drag soldering machine manufacturer. For years they attempted to devise a method of soldering surface mount devices via the drag soldering machine. Bridging was the largest problem along with component damage due to ex
Electronics Forum | Fri May 22 10:43:23 EDT 1998 | Mike Konrad
You're right Earl� Drag soldering is a dead issue as far as new technology is concerned. They do, however, work for most through-hole boards� but so do wave machines. There are only two manufacturers left that still produce drag soldering machine