Electronics Forum | Wed Jul 09 15:15:52 EDT 2008 | grics
Out of curiousity... What is the benefit of the selective solder machine that does NOT have a moveable nozzel? I am curious since this can be accomplished using a wave pallet. Thanks
Electronics Forum | Thu Jul 10 13:34:43 EDT 2008 | rwyman
We have a Vitronics mySelective machine (model 6749, or "the Fat Bastard" as we affectionately call it). It's configurable with various combinations of "select wave" and "multi wave" pots. Ours has one of each. The "select wave" is for the most pa
Electronics Forum | Wed Jul 09 14:57:42 EDT 2008 | ck_the_flip
I think what Chunks meant is... TOOLING = THOSE POTS So basically, if some of your SMT or Through-Hole parts move around via a redesign or a respin, you will incur tooling costs (TOOLING is "THOSE LITTLE POTS FULL O' SOLDER.") When you're research
Electronics Forum | Mon Aug 09 20:47:21 EDT 2004 | KEN
I think OA flux left on the pot would quickly looses its activity and become part of the dross waste stream, and smoke stream for that matter. Also, if your wave is setup properly your selective pallets will scour (push) the top of the lambda wav
Electronics Forum | Mon Aug 09 11:34:25 EDT 2004 | Woodsmt
I am looking for data / info on how flux may contaminate the solder in a Wave. I have a customer who requires a no clean process. Our wave is equipped with 2 separate fluxing systems and I would like to use OA in one and the No Clean in the other. Th
Electronics Forum | Tue Oct 21 16:18:35 EDT 2008 | nickh
Hey all, I'm looking for a place to get the solder from my wave flow tested, any suggestions? Thanks!
Electronics Forum | Wed Mar 15 11:34:28 EDT 2023 | proceng1
I'm sure this isn't the same situation, but we did have a selective solder machine with crazy dross and solder ball build up. Turns out the operator switched the low pressure nitrogen line used for solder level and the high pressure nitrogen line fo
Electronics Forum | Mon Mar 13 21:21:40 EDT 2023 | joeljacobo
Hello colleagues, I appeal to your expertise in this matter that has taken me by surprise. A week ago it was decided to change the solder brand for the wave machine, (only the brand, the alloy is the same). The pot was emptied and filled with the
Electronics Forum | Thu Oct 23 13:05:12 EDT 2008 | slthomas
If you're questioning their motivation for testing accurately, I'm sure they would *love* to sell you stuff to balance your alloy composition ratios or just replace all of your solder outright. IOW, I don't think you need to worry about them paddin
Electronics Forum | Tue Dec 13 06:56:27 EST 2005 | adanhn
Hi Steve, What I came up with for our Soltec Sigma 6621 is to make a stainless steel wave solder bath insert.The insert with all its components eg. impeller, Chipwave assy, pump shafts, main wave assy etc. I will send for plasma nitride coating.Afer